Leveling Polythene Co. Ltd

hebei, China

• MOQ 1 Ton

We offer Low Density Polyethylene and High-density polyethylene. Specification of hdpe for cable insulation property unit specification test melt flow index g/10min ≤0.4 astm d1238 density g/cm3 0.92-0.945 astm d1505 tensile strength mpa ≥13.0 astm d638 elongation at break % ≥500 astm d638 brittle temperature at low temperature °c ≤-76 astm d746 escr , fo h ≥96 astm d1693 oxidation induction period at 200°c min -- -- content of carbon black % -- -- carbon black dispersion -- ≥6 gb2951 absorption coeffcient -- ≥400 ceka softening point °c -- astm d1525 dielectric strength mv/m ≥25 astm d149 volume resistivity ω.m ≥1*1014 astm d257 dielectric constant -- -- astm d1505 packaging details: 25kg/bag, kraft paper bags with plastic bags inside delivery time: 15 days.

• MOQ 1 Ton

We offer Medium Density Polyethylene. Property test method test condition unit data melt index astm d1238 190â°c 2.16kg g/10min 6 density astm d1505 - g/ 0.936 tensile strength(yield) astm d638 50mm/min kg/ 160 tensile strength(break) astm d638 50mm/min kg/ 200 elongation (break) astm d638 50mm/min % 950 flexural modulus astm d747 - kg 6000 izod impact strength(notched) astm d256 23â°c kgâ·cm/cm 55 shore hardness astm d2240 23â°c d scale 62 vicat softening point astm d1525 1kg â°c 112 escr astm d1693 f:50% hrs > 500

• MOQ 1 Ton

We offer High Density Polyethylene. 1, used for insulation material of aerial cable, control cable of 1kv and below and similar situation. 2, highest temperature 70 specification of hdpe for cable insulation property unit specification test melt flow index g/10min â�¤0.4 astm d1238 density g/cm3 0.92-0.945 astm d1505 tensile strength mpa â�¥13.0 astm d638 elongation at break % â�¥500 astm d638 brittle temperature at low temperature â°c â�¤-76 astm d746 escr , fo h â�¥96 astm d1693 oxidation induction period at 200â°c min -- -- content of carbon black % -- -- carbon black dispersion -- â�¥6 gb2951 absorption coeffcient -- â�¥400 ceka softening point â°c -- astm d1525 dielectric strength mv/m â�¥25 astm d149 volume resistivity î©.m â�¥1*1014 astm d257 dielectric constant -- -- astm d1505 packaging details: 25kg/bag, kraft paper bags with plastic bags inside

• MOQ 1 Ton

property unit specification test melt flow index g/10min â�¤2.0 astm d1238 density g/cm3 â�¤0.945 astm d1505 tensile strength mpa â�¥14.0 astm d638 elongation at break % â�¥600 astm d638 brittle temperature at low temperature â°c â�¤-76 astm d746 escr , fo h â�¥500 astm d1693 content of carbon black % 2.60â±0.25 astm d1603 carbon black dispersion -- â�¤3 gb2951 absorption coeffcient -- â�¥500 ceka softening point â°c -- astm d1525 dielectric strength mv/m â�¥25 astm d149 volume resistivity î©.m â�¥1*1014 astm d257 dielectric constant -- â�¤2.80 astm d1505 it has excellent weather/wear resistance, toughness, and splendid resistance to environmental stress cracking, good processing performance and flexibility as well.

• MOQ 1 Ton

low density polyethylene(ldpe) 3840 rotating grade melt index:5 density:0.938 tensile strength at yield:150 hardness:60 elongation at break:1000% melting point:125 color:clear grade:prime