Rajkot, Gujarat, India
Verified
Add Review
Our Products
Specification
| Sr. no | Wire Diameter(mm) | Diameter Tolerance(mm) | Wire Grade | Tensile Strength(N/mm 2) | Elongation(%) | Available Spool Types |
|---|---|---|---|---|---|---|
| 1 | 0.10 | +0,-0.002 | Soft Semi Hard | 450-550 550-750 >980 |
>25 >10 <3 |
P5, DIN 125, DIN 160, Japax |
| 2 | 0.15 | +0,-0.002 | Soft Semi Hard | 450-550 550-750 >980 |
>25 >10 <3 |
P5, DIN 125, DIN 160, Japax |
| 3 | 0.20 | +0,-0.002 | Soft Semi Hard | 450-550 550-750 >980 |
>25 >10 <3 |
P5, DIN 125, DIN 160, Japax |
| 4 | 0.25 | +0,-0.002 | Soft Semi Hard | 450-550 550-750 >980 |
>25 >10 <3 |
P5, DIN 125, DIN 160, Japax |
| 5 | 0.30 | +0,-0.002 | Soft Semi Hard | 450-550 550-750 >980 |
>25 >10 <3 |
P5, DIN 125, DIN 160, Japax |
| ALLOY CODE: A1 - CuZn40, A2 - CuZn37, A3 – CuZn3S | ||||||
SPECIAL FORGING BRASS RODS FOR VALVES IS 8737 / AMD – 2
| Chemical Requirements % | |
|---|---|
| Copper | 56.5 - 60.0 % |
| Lead | 1.0 - 2.0 % |
| Manganese | 0.50 % max. |
| Iron | 0.30 % max. |
| Total Imp. | 0.75% max. |
| Zinc | Remainder |
.
| Physical Properties | |
|---|---|
| Tensile Strength | 40 kg/mm2 Min |
| Elongation % | 18% Min. |
| Izod Value | 2.2 Kgf Min. |
Properties
| Physical Property | ||
| Properties | Metric | Imperial |
| Density | 10.3 gicm3 | 0.369 lb/in3 |
| Melting point | 2625°C | 4760°F |
| Mechanical Properties | ||
| Properties | Metric | Imperial |
| Tensile strength (annealed) | 324 MPa | 47000 psi |
| Shear strength (torsional strain rate 0.25/s) | 500 MPa | 72500 psi |
| Compressive yield strength (0.01% yield) | 400 MPa | 58000 psi |
| Modulus of elasticity | 330 GPa | 47900 ksi |
| Modulus of elasticity at elevated temperature (@2000°C/3630°F) | 160 GPa | 23200 ksi |
| Thermal Coefficient of Expansion: | 5 x 10-6 cm/cm @ 25 oC | |
| Electrical Conductivity: | 34% I.A.C.S. | |
| Thermal Conductivity: | 1.38 W/cm/K @ 298.2 K | |
| Electrical Resistivity: | 5.2 microhm-cm @ 0 oC | |
Properties
| Physical Property | ||
| Properties | Metric | Imperial |
| Density | 10.3 gicm3 | 0.369 lb/in3 |
| Melting point | 2625°C | 4760°F |
| Mechanical Properties | ||
| Properties | Metric | Imperial |
| Tensile strength (annealed) | 324 MPa | 47000 psi |
| Shear strength (torsional strain rate 0.25/s) | 500 MPa | 72500 psi |
| Compressive yield strength (0.01% yield) | 400 MPa | 58000 psi |
| Modulus of elasticity | 330 GPa | 47900 ksi |
| Modulus of elasticity at elevated temperature (@2000°C/3630°F) | 160 GPa | 23200 ksi |
| Thermal Coefficient of Expansion: | 5 x 10-6 cm/cm @ 25 oC | |
| Electrical Conductivity: | 34% I.A.C.S. | |
| Thermal Conductivity: | 1.38 W/cm/K @ 298.2 K | |
| Electrical Resistivity: | 5.2 microhm-cm @ 0 oC | |
Specification
| Sr. no | Wire Diameter(mm) | Diameter Tolerance(mm) | Wire Grade | Tensile Strength(N/mm 2) | Elongation(%) | Available Spool Types |
|---|---|---|---|---|---|---|
| 1 | 0.10 | +0,-0.002 | Soft Semi Hard | 450-550 550-750 >980 |
>25 >10 <3 |
P5, DIN 125, DIN 160, Japax |
| 2 | 0.15 | +0,-0.002 | Soft Semi Hard | 450-550 550-750 >980 |
>25 >10 <3 |
P5, DIN 125, DIN 160, Japax |
| 3 | 0.20 | +0,-0.002 | Soft Semi Hard | 450-550 550-750 >980 |
>25 >10 <3 |
P5, DIN 125, DIN 160, Japax |
| 4 | 0.25 | +0,-0.002 | Soft Semi Hard | 450-550 550-750 >980 |
>25 >10 <3 |
P5, DIN 125, DIN 160, Japax |
| 5 | 0.30 | +0,-0.002 | Soft Semi Hard | 450-550 550-750 >980 |
>25 >10 <3 |
P5, DIN 125, DIN 160, Japax |
| ALLOY CODE: A1 - CuZn40, A2 - CuZn37, A3 – CuZn3S | ||||||
FREE CUTTING & FORGING BRASS RODS EN 12164: 1998
| A | B | |
|---|---|---|
| Chemical | CuZn39Pb3 | CuZn40Pb2 |
| Requirement(%) | CW614N | CW617N |
| Copper | 57-59 | 57 - 59 % |
| Lead | 2.5 - 3.5 % | 1.6 - 2.5 |
| Aluminum | 0.05 % max | 0.05 % max |
| Iron | 0.30 % max | 0.30 % max |
| Nickle | 0.30 % max | 0.30 % max |
| Tin | 0.30 % max | 0.30 % max |
| Total Imp. | 0.20 % max | 0.20 % max |
| Zinc | Remainder | Remainder |
Physical Properties (1/2 Hard)
| Condition | Size | T. S. Mpa | EL % Min | Size | T. S. Mpa | EL % Min |
|---|---|---|---|---|---|---|
| Half-Hard (AB) | 6 -14 | 400 | 15 | 6 -14 | 550 | |
| 14-40 | 380 | 18 | 14-40 | 500 | 8 | |
| 40 -80 | 360 | 20 | 40 -80 | 430 | 10 |
FREE CUTTING BRASS RODS - GRADE I
| Chemical Requirements (%) | Grade I |
|---|---|
| Copper | 56.0 - 59.0 % |
| Lead | 2.0 - 3.50 % |
| Iron | 0.35% max. |
| Total Imp. Excl. Iron | 0.70% max. |
| Zinc | Remainder |
Physical Properties Grade I
| Condition | Size | T. S. MPA | EL % Min |
|---|---|---|---|
| Annealed 10) | 6-25 | 345 | 12 |
| 25-50 | 315 | 17 | |
| 50 above | 285 | 22 | |
| Half-Hard (HB) |
6-12 | 405 | 4 |
| 12-25 | 395 | 6 | |
| 25-50 | 355 | 12 | |
| Hard (HD) | 50 above | 325 | 17 |
| 6-12 | 550 | - | |
| 12-25 | 490 | 4 |
Chemical
| Requirements(%) | Grade II | Grade III |
|---|---|---|
| Copper | 60.0 - 63.0 % | 60.0 - 63.0 % |
| Lead | 2.50 - 3.70 % | 0.50 - 1.50 % |
| Iron | 0.35 , max. | 0.20 % max. |
| Total Imp. Excl. Iron | 0.50 % max. | 0.50 % max. |
| Zinc | Remainder | Remainder |
Physical Properties Grade II Grade III
| Condition | Size | T. S. MPA | EL % Min | T. S. MPA | EL %Min |
|---|---|---|---|---|---|
| Annealed (0) | 6-25 | 355 | 15 | 315 | 22 |
| 25-50 | 305 | 20 | 285 | 27 | |
| 50 above | 275 | 25 | 255 | 32 | |
| Half-Hard (H8) |
6-12 | 395 | 7 | 355 | 8 |
| 12-25 | 385 | 10 | 345 | 12 | |
| 25-50 | 345 | 15 | 305 | 22 | |
| Hard (HD) | 50 above | 315 | 20 | 285 | 27 |
| 6-12 | 550 | - | 460 | - | |
| 12-25 | 485 | 4 | 400 | 4 |
JR3A Ointment Vinon Technology Industrial Co., Ltd.
| Proportion | Put the liquid Into running water with a ratio 1:40 - 50 (avoid hard water such as well water or ground water, |
|---|---|
| Ingredients | Green product for the environment |
| Using range | Applied to all types of Wire-cutting Electric Discharge machine. It can be also used as cooling liquid for metal-cutting processes. |
| Features | This product has excellent cleaning performance, suitable for high thickness cut and multiple-cut, dissolves quickly, and shipping conveniently. The main matched machine tool now is exported to international market |
| 1. High ratio. dissolves quickly, use conveniently. 2. Uniform and white finish surface without black & white stripe normally seen (cleaned by kerosene). 3 The product has great cutting stability under large energy condition (average processing current over 5A), compared with the traditional emulsified oil, cutting efficiency increased by 30%, surface finish degree improvement half grade, electrode wire loss reduced by 50% and. molybdenum wire life is greatly extended. 4. Workpiece is easy to take off and clean, and the workbench is also clean. 5. Suitable for cutting within 500mm thickness die steel, it is also suitable for maltiple-cut. |
|
| Expiry Date | 12 Months |
| Package | 2KG Special Plastic Bottle. 181:0130X, (2.9 bottles) |
| Precautions and appearance | 1. The primary liquid is yellow and the diluted liquid is light milky white. This product has excellen1 cleaning performance. add the primary liquld and water in proportion when replenishing liquid. 2. Please use the magnet to suck the workpiece before processing is finished, and avoid breaking molybdenum wire. |
| Quality standard | Q/ZJRX 001-2004 |
JRIA WEDM Composite Liquide
| Proportion | Put the liquid Into running water with a ratio 1:12 - 15 (avoid hard water such as well water or ground water, |
|---|---|
| Ingredients | Green product for the environment |
| Using range | Applied to all types of Wire-cutting Electric Discharge machine. It can be also used as cooling liquld for metal-cutting processes. |
| Features | 1.Uniform and white finish surface .thout black & Mfite stripe normally seen (cleaned by kerosene). 2.Suitable for large current cutting (over 3.5A In ordinary machine tools, over 5A in WEDM-MS), compared with the traditional emulsified oil , cutting efficiency increased by 30%, surface finish degree improvement half grade, electrode wire loss reduced by 50% and molybdenum wire life is greatly extended. 3.Workplece Is easy to take off and clean the workbench is also clean. 4.Suitable for cutting within 500mm thickness die steel. it is also suitable for multiple-cut. |
| Expire Date | 12 Months |
| Packege | Liquid using steel bucket (18 KG) |
| Precautions and appearance | 1. The primary liquid is yellow and the diluted liquid is light milky white. This product has excellen1 cleaning performance. add the primary liquld and water in proportion when replenishing liquid. 2. Please use the magnet to suck the workpiece before processing is finished, and avoid breaking molybdenum wire. |
| Quality standard | Q/ZJRX 001-2004 |