Chemical Composition (wt%):
Elements | Chemistry % | |||
Copper Alloy UNS C17200 | ||||
C17000 | C17200 | C17300 | ||
Be | 1.60-1.79 | 1.80-2.00 | 1.80-2.00 | |
Ni+Co,≥ | 0.2 | 0.2 | 0.2 | |
Ni+Co+Fe,≤ | 0.6 | 0.6 | 0.6 | |
Al,≤ | 0.2 | 0.2 | 0.2 | |
Si,≤ | 0.2 | 0.2 | 0.2 | |
Pb | / | / | 0.20-0.60 | |
Cu | Remainder | Remainder | Remainder |
Chemical composition:
C % | Si % | Mn % | Cr % | Al % | Fe % | |
---|---|---|---|---|---|---|
Nominal composition | 5.8 | Bal. | ||||
Min | - | - | - | 20.5 | - | |
Max | 0.08 | 0.7 | 0.4 | 23.5 | - |
Mechanical properties:
Wire size | Yield strength | Tensile strength | Elongation | Hardness |
---|---|---|---|---|
Ø | Rp0.2 | Rm | A | |
mm | MPa | MPa | % | Hv |
1.0 | 545 | 760 | 20 | 240 |
4.0 | 475 | 680 | 18 | 230 |
Mechanical properties at elevated temperature:
Temperature °C | 900 | 1000 | 1100 | 1200 | 1300 |
---|---|---|---|---|---|
MPa | 34 | 18 | 10 | 6 | 4 |
Creep strength - 1% elongation in 1000 h:
Temperature °C | 800 | 1000 |
---|---|---|
MPa | 1.2 | 0.5 |
Young's modulus:
Temperature °C | 20 | 100 | 200 | 400 | 600 | 800 | 1000 |
---|---|---|---|---|---|---|---|
GPa | 220 | 210 | 205 | 190 | 170 | 150 | 130 |
Temperature factor of resistivity:
Temperature°C | 100 | 200 | 300 | 400 | 500 | 600 | 700 | 800 | 900 | 1000 | 1100 | 1200 | 1300 | 1400 |
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
Ct | 1.00 | 1.00 | 1.00 | 1.00 | 1.01 | 1.02 | 1.02 | 1.03 | 1.03 | 1.04 | 1.04 | 1.04 | 1.04 | 1.05 |
The coefficient of thermal expansion:
Temperature °C | Thermal Expansion x 10-6/K |
---|---|
20 - 250 | 11 |
20 - 500 | 12 |
20 - 750 | 14 |
20 - 1000 | 15 |
Thermal conductivity:
Temperature °C | 50 | 600 | 800 | 1000 | 1200 | 1400 |
---|---|---|---|---|---|---|
W m-1 K-1 | 11 | 20 | 22 | 26 | 27 | 35 |
Specific heat capacity:
Temperature °C | 20 | 200 | 400 | 600 | 800 | 1000 | 1200 | 1400 |
---|---|---|---|---|---|---|---|---|
kJ kg-1 K-1 | 0.46 | 0.56 | 0.63 | 0.75 | 0.71 | 0.72 | 0.74 | 0.80 |