• General PropertiesMinimum Value for conformity
• Moisture contentNot more than 20%
• Density750-800 kg/m2
• Flammability testTime taken for second ignition shall not be less than 30 minutes
• Flame penetrationMinimum 30 minutes for 12mm
• Rate of burning testMinimum 20 minutes
• Glue adhesion & Water Resistance Test (cyclic test followed by knife test) i.e. cycle of 8 hours boiling and 16 hours drying at 65± 2ºC (as per IS : 303)Minimum standard pass after 3cycles
• Static bending strength (as per IS : 303)\r\n \r\n 1. Modulus of rupture\r\n \r\n (a) Along the grain\r\n \r\n \r\n (b) Across the grainMin Ind.:- 36N/MM2\r\n Avg.:- 40 N/M2\r\n \r\n Min Ind.:- 18N/MM2\r\n Avg.:- 2500 N/M2
• Resistant to micro organisms (after 21 days) test for adhesion of ply (as per IS : 303)Minimum Standard Pass

• Test prescribedObserved Value
• Tensile strength380 psi
• Crush strength300 psi
• Acoustics35 STC (Sound Transmission Class)
• Eco-FriendlyRecyclable Kraft paper impregnated with special polymers
• Weight40 % lower weight than solid doors
• Moisture content (%)For maximum pressure strength, the moisture content is kept between 8 – 10 %
• Slam test1,000,000 Cycles. Grade 1 without failure
• Twist/Torque TestMax deflection At 300# + .800”max, permanent set + .029”
• Insulation properties“U” Factor :0.041\r\n “R” Factor : 2.44

BWP Flush Door is extremely durable thanks to its excellent quality, exceptional finish and unique dimensional stability. It is made of a single select hardwood species and bonded with boiling water proof synthetic phenol formaldehyde adhesive. Its hardwood frames provide strength for fitting of hinges. These doors provide assure strength and safety, and therefore guarantee peace of mind.

• TESTSPARAMETERS
• TimberOnly Dipterocarpus species
• Density of plywoodApprox 825kg/m3
• AdhesiveUnextended undiluted BWP Type conforming to IS 848 : 1974
• Preservative treatmentAll logs are cooked to remove starch & to kill micro-biological organisms.\r\n Glue line is fortified with CCP treatment.\r\n Finished panels are treated with CCB method.
• Veneer\r\n a) Selection\r\n \r\n \r\n b) Density\r\n \r\n \r\n c) Treatment\r\n \r\n \r\n Veneer to Veneer ratioSAP portion of veneers are segregated and only class 1 durable veneers are used\r\n Since single species of timber is used, the density of all veneers remains the same\r\n \r\n Veneers are treated with preservatives\r\n \r\n \r\n Max 1:2
• BondingGuranteed for lifetime
• DurabilityExcellent and extra durable
• Face thickness1.00 mm
• BIS relevanceExceeds all parameters
• Moisture content(%)8-12%

•  \\
• TESTSPARAMETERS
• Thickness available (mm)All thickness (generally 12mm is used)
• Dimension available (mm X mm)Max. 2440 x1220
• Density (Kg/m3)800
• Boil cyclePass (72hrs boiling)
• Moisture content (%)8-10%
• Water resistance> 100
• Glue shear strength (kg) – Dry> 135
• Glue shear strength (kg) – Mycological> 100
• Adhesion of plyExcellent
• Water absorption test< 5%
• Screw holding strength (kg)> 275
• Nail holding strength (kg)150
• Static bending strength 
• MoR (N/mm2) 
• Across the grain> 4000
• Along the grain> 7500
• MoE (N/mm2) 
• Tensile strength\r\n \r\n Along the grain\r\n \r\n Across the grain\r\n \r\n Sum of Both325 kgf/cm2\r\n \r\n 225 kgf/cm2\r\n \r\n 600 kgf/cm2
• Preservative treatment 
• Glue lineCCP treatment
• Preservation chemical retention/ treatment 

• TESTSPARAMETERS
• MOR90 N
• MOE8600 N
• Screw holding (IS : 1734)1250 N
• Nail withdrawal (IS :1734)950 N
• Bending Diameter4mm
• 6cm 
• 6mm10cm
•  8mm
• 20cm 
• 12mm38cm