Grade |
The impurity content is not more than % | |||||||
| Fe | Ni | Al | Si | Mg | C | N | O | |
| Mo-1 | 0.01 | 0.005 | 0.002 | 0.01 | 0.005 | 0.01 | 0.003 | 0.008 |
| Mo-2 | 0.01 | 0.005 | 0.005 | 0.01 | 0.005 | 0.01 | 0.003 | 0.02 |
| Grade B.S. 1400: 1985 | Nominal Composition | 2% PS N/mm Min | Tensile Strength N/mm Min | Elongation % Min | Brinell Hardness Min |
| G1/BC3 | 32418 | 245 | 15 | — | |
| G1/BC2 | 32359 | 245 | 20 | — | |
| LG1 | 88/3/9/5 | 85 | 180 | 15 | 60 |
| LG2 | 85/5/5/5 | 90 | 200 | 13 | 60 |
| LG3 | 86/7/5/2 | — | — | — | — |
| LG4 | 88/7/2/3 | 130 | 230 | 14 | 65 |
| BC1 | 82/3/10/5 | — | 165 | 15 | — |
| BC6 | 85/5/5/5 | — | 215 | 18 | — |
| Grade | Zr+Hf | Hf | Fe+Cr | Sn | H | N | C | O | Nb |
| R60702 | 99.2% | <4.5% | <0.20% | – | <0.005% | <0.015% | <0.030% | <0.15% | – |
| R60704 | 97.5% | <4.5% | 0.2-0.4% | 1.0-2.0% | <0.005% | <0.015% | <0.030% | <0.16% | – |
| R60705 | 95.5% | <4.5% | <0.2% | – | <0.005% | <0.015% | <0.050% | <0.16% | 2.0-3.0% |
| Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
| 8.1 g/cm3 | 1443 °C (2430 °F) | Psi – 80000 , MPa – 551 | Psi – 35000 , MPa – 241 | 30 % |
| Grade | DIN | UNS | SUS |
| ASTM A182 F1 | 1.5415 | K12822 | 16Mo3 |
| ASTM A182 F44 | 1.4547 | S31254 | |
| ASTM A182 F51 | 1.4462 | S31803 | SAF 2205 |
| ASTM A182 F52 | S32950 | ||
| ASTM A182 F53 | 1.4410 | S32750 | SAF 2507 |
| ASTM A182 F55 | 1.4501 | S32760 | Zeron 100 |
| ASTM A182 F60 | 1.4462 | S32205 | |
| ASTM A182 F61 | 1.4507 | S32550 | Ferralium 255 |