Coated Fiberglass Rovings

  • Material E-glass Fiber With Proprietary PU Resin Systems
  • Feature High Strength, Softness, Flexibility, Light Weight, High Productivity
  • Packaging Type Long Continuous Lengths
  • Storage Type Dry And Protected From Direct Sunlight
  • Linear Density 610 Gm/Km To 2450 Gm/Km
  • Tensile Strength At Break 370 N To 1470 N
  • Modulus Of Elasticity 76400 N/mm²
  • Elongation At Break 3.5%
  • Strand Width (Avg.) 2.3 Mm To 4.5 Mm
  • Strand Thickness 0.15 Mm To 0.36 Mm

Product ApplicationSRIF LEX OF is a very high strength coated glass roving for optical fiber and copper cables. It is most suited for uni-tube, loose tube & slotted core cables & typically used as peripheral reinforcement in fibre optic cables along with FRP Rod & Serni-Rigid FRP Rods. lt is introduced over the loose tube and the cable manufactured with it would be lower in diameter, lighter in weight with high degree of flexibility, excellent tensile strength & modulus performance. DescriptionSRIFLEX OF is manufactured using E-glass fibre with proprietary PU resin systems to produce an innovative, value added reinforcement solution with high degree of softness and strength. It has a special smooth, flexible coating which improves handling and eliminates dust and loose fiber generation during cable production, even at very high speeds, leading to high productivity and ultimate cable strength. The soft fiber spread evenly on the cable core minimize thickness build-up. lt is available in long continuous lengths for enhanced productivity. It has a very high strength to weight ratio resulting in light weight cable with utmost ease of handling. It is available in long continuous lengths with tex (gm/Km) ranging from 600 tex to 2400.

Specifications

 

High Strength Grade - HS - SRI-625 SRI-750 SRI-1225 SRI2450 Test Method
Physical Properties Unit Value Value Value Value
Linear Density, Tex gm/Km 610 750 1225 2450 ASTM D-578
Tensile Strenght at Break N 370 450 734 1470 ASTM D-885
LASE @ 0.5% Elognation N 81 105 160 313 ASTM D-885
LASE @ 1.0% Elognation N 170 224 334 654 ASTM D-885
Modulus of Elasticity N/mm² 76400 76400 76400 76400 ASTM D-885
Elognation at Break % 3.5 3.5 3.5 3.5 ASTM D-4963-94
Strand Width (Avg.)(Dry) mm 2.3 2.5 2.8 4.5 ASTM D-885
Strand Thickness (Dry) mm 0.15 0.2 0.26 0.36 ASTM D-885
View Complete Details

Yellow Polyester Rip Cord

  • Country of Origin India
  • Type Industrial Yarn
  • Color Yellow
  • Twist Type Double Twist
  • Material Polyester
  • Pattern Plain
  • Packaging Type Roll
  • Diameter 1-10mm, 10-20mm

Ripcord is made of polyester used for easy removal of the cable jacket Ripcords can be used in almost any type of cable, providing easy access to the cable core during installation or maintenance. Due to using high tenacity base polyester and the high quality of the twisting, Polyester ripcord can cut through some corrugated steel tapes. We supply customised types and lengths to cable manufacturers world-wide. Product is available in White, Yellow and in Combination of Colour. Also can be made as per requirement of client. All Ripcoeds are available in Wickning & Non Wickning

Specifications

 

Physical Properties Unit Product ID Test Method
SRI-2250/3 SRI-3000/3 SRI-6000/3
Linear Density Denier / Dtex 2250/2500 3000/3300 6000/6000 ASTM-885
Product Description - 750x3PLY 1000x3PLY 2000x3PLY -
Breaking Load Kgs >14 >22 >42.0 ASTM-2256
Shrinking % <10.0 ASTM-2259
Elogation % 15% Min 15% Min 15% Min ASTM-2256
swelling Speed ml/gm/1 min NA NA NA ICPL/Y/002
swelling Height ml/gm/5 min NA NA NA ICPL/Y/003
Nominal Yield m/kg 3750 2600 1400 -