S-Bond Technologies, LLC

S-Bond® 140 is lower temperature active solder that melts from 135 – 140°C. The solder, is based around the Bismuth-Tin (Bi-Sn) eutectic composition. This solder enables multi-step soldering where previously soldered connectionsseals are not remelted. Applications are in thermally sensitive applications where Sn-Ag based solders that melt over 215°C can thermally degrade the component parts being assembled. Lower temperature soldering also can more effectively bond dissimilar materials where thermal expansion mismatch many times fractures or distorts an assembly’s component parts. S-Bond 140 is being used in LED packages, glass-metal seals in electronic packages where higher temperature soldering alloys would have damaged the packages’ components, heat pipes and vapor chambers that have been charged with phase change materials that cannot be exposed to temperatures over 200°C. - See more at: http:www.s-bond.comproductsnew-s-bond-140-alloy#sthash.95huM5mJ.dpuf

S-Bond Technologies offers a series of different Kits as a way to experiment with the use of our S-Bond materials in applications. Each kit provides choice of our S-Bond alloys and a CD manual outlining how best to apply and activate the material. Other kits offer tools for mechanically activate the S-Bond alloys. More advanced kits offer additional tools for conducting joining tests, such as hot plates, and telephoneemail application engineering assistance. Please Contact Us for information on pricing and delivery of… Test Kits: this kit provides a smaller amount of S-Bond alloy for customers to evaluate the alloys in their application. Introductory Kits: this kit contains additional material and common tools for applying the materials. Standard Kits: this kit is for experienced customers seeking to develop a specific application and need additional tools. Deluxe Kits: a complete kit with all of the tools needed to do S-Bond® joining right from the box, including hot plate (for US power only) - See more at: http:www.s-bond.comproductskits#sthash.ZQJpbehr.dpuf