Our Products
Talc is a hydrous magnesium silicate, (3MgO-4SiO2-H2O) when found in pure form. Talc is used as flux for high alumina Ceramics, Sanitaryware and Dinnerware. It is a low cost source of magnesium in these applications and helps to produce less porous bodies at lower firing temperature.
We produce TALK in forms of :
1 Powder (150-25 microns)
2. LUMPS
Packing :Standard Packing available in 50 kg. HDPE bags & 500 KG , 1 or 1.25 MT. Jumbo bags with liner inside, or as per customer requirements
Technical Specification
Analyte | Talc a | Talc b |
---|---|---|
SiO2 | 62.00% (± 01.00%) | 61.00% (± 01.00%) |
MgO | 31.00% (± 02.00%) | 28.00% (± 01.00%) |
CaO | 01.00% (± 00.50%) | 03.00% (± 01.00%) |
Fe2O3 | 00.50% (± 00.10%) | 00.50% (±00.10%) |
LoI @ 1000oC | 05.00%(± 01.00%) | 06.50% (± 01.00%) |
Ph | 09.00% (± 00.50%) | 09.00% (± 00.50%) |
Brightness | 88.00% (± 00.50%) | 82.00% (± 01.00%) |
SODIUM FELDSPAR (NA-SPAR)
In ceramic bodies, the main vitrifying (fluxing) agent is feldspar. The majority of white ware bodies contain good proportions of feldspar. It acts as a flux. In the ceramic industry, the flux is defined as that portion of the body which develops glass phase. This is provided mostly by feldspar. The amount of flux in a ceramic body should be only in such a proportion as to develop the desired amount of vitrification. If excess of flux is added, the fired body becomes very glassy and consequently, brittle.
The glass and ceramic industries are the major consumers of feldspar and account for 95% of the total consumption.
Feldspar is generally used for three purposesIn making the body composition of several types of procelain, china and earthenware and also in the preparation of glazes and enamel. As an important ingredient in the glass sand batch. As a bonding agent in the manufacture of bonded abrasives like wheels and discs of garnet, corundum, emery etc
We produce SODIUM FELDSPAR(NA-SPAR) in forms of :1. Granular Particles2. Powder (150-25 microns)3. Lumps form 1 inches to 15 inches
Standard Packing available in 50 kg HDPE bags and 1or 1.25 m t Jumbo bags with liner inside , or as per customer requirements.
Specifications - Grade (N -SPAR - 1)
SiO2 | % | 67.48 |
Al2O3 | % | 18.5 |
K2O | % | 0.82 |
Na2O | % | 09.24 |
Fe2O3 | % | 0.07 |
CaO | % | 0.34 |
MgO | % | NIL |
Specifications - Grade (N -SPAR - 2)
SiO2 | % | 68.84 |
Al2O3 | % | 17.5 |
K2O | % | 0.82 |
Na2O | % | 07.01 |
Fe2O3 | % | 0.12 |
CaO | % | 0.44 |
MgO | % | NIL |
WE ARE LEADING MANF. AND EXPORTERS OF HIGH PURITY FELDSPAR FROM INDIA SINCE 1971 ., RECENTLY WE INSTALLED WORLD HIGH TECH PLANTS WITH DAILY CAPACITY 550 MT .
Additional Information:
Payment Terms : L/C, D/P
Packaging Details : WE CAN MAKE PACKING AS PER CUSTOMERS REQUIRMENTS WITH 50 KGS HDPE BAGS , 25 KGS PAPER BAGS , 1250 KGS JUMBO BAGS
Delivery Time : 20 DAYS
Additional Information:
Payment Terms : L/C, D/P
Delivery Time : 10 DAYS
Additional Information:
Packaging Details : WE CAN MAKE PACKING AS PER CUSTOMERS REQUIRMENTS WITH 50 KGS HDPE BAGS , 25 KGS PAPER BAGS , 1250 KGS JUMBO BAGS
Additional Information:
Packaging Details : WE CAN MAKE PACKING AS PER CUSTOMERS REQUIRMENTS WITH 50 KGS HDPE BAGS , 25 KGS PAPER BAGS , 1250 KGS JUMBO BAGS
In ceramic bodies, the main vitrifying (fluxing) agent is feldspar. The majority of white ware bodies contain good proportions of feldspar. It acts as a flux. In the ceramic industry, the flux is defined as that portion of the body which develops glass phase. This is provided mostly by feldspar. The amount of flux in a ceramic body should be only in such a proportion as to develop the desired amount of vitrification. If excess of flux is added, the fired body becomes very glassy and consequently, brittle.
The glass and ceramic industries are the major consumers of feldspar and account for 95% of the total consumption. Feldspar is generally used for three purposes
We produce POTASH FELDSPAR(K-SPAR) in forms of :
Standard Packing available in 50 kg HDPE bags and 1 or 1.25 M.T. Jumbo bags with liner inside , or as per customer requirements.
Specification
SiO2 | 67.50% (± 01.00%) | 69.50% (± 01.00%) | 72.50% (± 02.00%) |
Al2O3 | 17.75% (± 00.50%) | 17.05% (± 00.50%) | 15.50% (± 01.00%) |
K2O | 12.10% (± 00.60% | 10.00% (± 00.50%) | 08.00% (± 01.00%) |
Na2O | 02.50% (± 00.80%) | 02.50% (± 00.80%) | 02.75% (± 01.00%) |
Fe2O3 | 00.07% (± 00.01%) | 00.10 (± 00.02%) | 00.20 (± 00.05%) |
CaO | Nil | Nil | Nil |
MgO | Nil | Nil | Nil |
TiO2 | Nil | Nil | Nil |
LoI @ 1000oC | 0.10% | 0.10% | 0.10% |
Additional Information:
Payment Terms : L/C, D/P
Delivery Time : 10 DAYS
We supply high quality Kaolin Powder, processed in an ISO 9000:2001 certified plant that is well equipped with most sophisticated laboratory for stringent quality control. Kaolin Cf powder is available in various sizes and grades to match the several requirements of the clients. We have firmly positioned ourselves as one of the major white kaolin powder manufacturers and suppliers, based in India. Perfect for different industrial applications, our kaolin powder is highly reliable and proficient. Low impurity and high consistent quality are the unique characteristic of kaolin powder. Features
Grades
Standard Size
Specifications
CHEMICAL ANALYSIS | ||||
SiO2 | 47.12 | 47.12 | 45.70 | 45.22 |
Al2O3 | 36.86 | 36.86 | 38.12 | 37.78 |
Fe2O3 | 0.66 | 0.28 | 0.40 | 0.44 |
CaO +MgO | 0.31 | 0.16 | 0.16 | 0.43 |
TiO2 | 0.81 | 0.55 | 0.75 | 0.81 |
Na2O +K2 O | 0.92 | 0.58 | 0.10 | 0.85 |
L.O.I | 12.34 | 13.74 | 13.84 | 14.62 |
PHYSICAL PROPERTIES | ||||
Moisture w/w% (max) | 3.0 | 3.0 | 2 | 2 |
pH | 7 - 8 | 7 - 8 | 7.5 | 6 |
Suspension (% in 24 hours) | Good | Good | 85 | Good |
<2 micron w/w% (min) | 40 | 60 | 70 | 85 |
Water of Plasticity (ml/100gm) | 32 | 28 | ||
Water Absorption (%) | 30 | 14.2 | ||
+300 m retention w/w % | <1.0 | 0.5 | 0.3 | 0.1 |
Green Shrinkage (%) | 3.2 | 2.41 | ||
Fired Shrinkage (%) | 7.8 | 12.2 | ||
Natural Gloss % (min) | 83 | 90 | 85 | 85 |
Fired Gloss % (min) | 87 | 96 |
Additional Information:
Payment Terms : L/C, D/P
Packaging Details : Standard Packing available in 50 kg HDPE bags and 1 or 1.25 m t Jumbo bags with liner inside , or as per customer requirements.
Delivery Time : 10 DAYS
Applications :
As a filler in rubber, plastic, linoleum paper in paper coating, canvas white, shoe dressings, white ware, sealant, making of cement, as a flux in smelting metallic ores or alloys, as a fertilizer glass manufacturing, ceramics-glazes and enamels, cattle feed etc.
Packing :Standard Packing available in 50 kg. HDPE bags & 1 or 1.25 mt Jumbo bags with liner inside, or as per customer requirements.
Specification
Calcium Oxide CaO | 56.47 | 56.19 | 55.85 |
Calcium Ca | 40.36 | 40.16 | 39.91 |
Magnesium Oxide MgO | Traces | Traces | Traces |
Silica SiO2 | 00.30 | 00.52 | 01.38 |
Aluminium Al2O3 | 00.05 | 00.05 | 00.08 |
Ferric Oxide Fe2O3 | 00.04 | 00.04 | 00.06 |
Titanium Dioxide TiO2 | Nil | Nil | Nil |
Maganous Oxide MnO | Nil | Nil | Nil |
Pottasium Oxide K2O | 00.006 | 00.006 | 00.006 |
Phosphorous Pentoxite P2O5 | 00.007 | 00.009 | 00.011 |
Phosphorous P | 00.003 | 00.004 | 00.005 |
Sulphur Trioxide So3 | 00.012 | 00.02 | 00.03 |
Loss on Ignition L.O.I. | 43.38 | 43.12 | 42.44 |
Loss on Drying @ 105.C | 00.08 | 00.10 | 00.10 |
Chloride Cl | 00.02 | 00.02 | 00.02 |
Sulphates SO4 | 00.017 | 00.021 | 00.04 |
Alkali Water Solution | 00.02 | 00.02 | 00.12 |
Heavy Metals Pb | Nil | Nil | Nil |
Arsenic As | Nil | Nil | Nil |
Carbon-di-oxide CO2 | 43.30 | 43.02 | 42.34 |
Insoluble in water & alcohol | 99.90 | 99.96 | 99.91 |
Aluminium, Iron Phosphate and matter insoluble in hydrochloric acid | 00.43 | 00.73 | 01.91 |
Barium Ba | Nil | Nil | Nil |
Petroleum Ether extract | 00.36 | 00.09 | 0.04 |
Loss on Ignition @ 900C (after 30 minutes ) | 42.87 | 42.71 | 42.60 |
Oil Absorpton | 21.17 | 21.23 | 21.33 |
Calcium Carbonate (on as such basis) CaCO3 | 98.14 | 97.84 | 96.29 |
Calcium Carbonate ( on dry basis) CaCO3 | 98.67 | 97.94 | 96.38 |
Specific gravity | 02.60 | 02.71 | 02.80 |
pH ( of 10 % soluble) | 08.40 | 08.35 | 08.40 |
Bulk Density | gm/ml | gm/ml | gm/ml |
Additional Information:
Payment Terms : L/C, D/A, D/P
Packaging Details : AS REQUIRED
Delivery Time : 15 DAYS
Introduction:
The role of Acidic Ramming Mass in steel melting through induction Furnance is very important. Due to its important propÂerty to with stand thermal shocks without developing any cracks due to interrupted power supply which is the case through out our conutry We have taken initiative to develop acidic ramming mass of high quality silica Quartz having heavy dencity.
Product:
Our ramming mass is a product of super snow white crystalline quartz havmg 99.90% Silicon dioxide (sio2 ) and manufactÂured under strict quality control and calciÂned to eliminate the spal1ing tendancy in stabilized form, where silica neither exponds nor contracts It is suitable for with standing higher temperature upto l720oc
Specifications:
Sio2 - 99.90'/.Al2O3 - 0.02%
Free from Iron contents
Softerning Point : - 1280 C
Porosity : 50
Compression St : 350 Kg /CM2
Bulk Density : 2.00 to 2.2 Ton/M3
PCE Value ASTN No : 31-32
Important Features:
o
o
o
o
OUR ACIDIC RAMMING MASS
Application :
Packing :