Instructions for Use : The material shall be semi-stiff, smooth and homogenous paste suitable for application by spreading with hand or trowel or spatula at temperatures not less than 27oC. Use compatible JAI Primer to paint the cracks.
Surface Preparation : The surface should be free from dust, grease, rust and loose particles.
Specification
Characteristic | Requirements |
---|---|
Water content, % by wt., Max | 0.5 |
Ash content % by wt. | <40 |
Flow | Shall satisfy the requirement |
Flash point, oC, Min. | 35 |
Flexibility & Adhesion | - |
Consistency | Soft paste / semi solid |
Hydrostop is the ideal membrane for use as :
Special Features :
Specification
Characteristics | Requirement | Test |
---|---|---|
Softening Point oC | 150 | ASTM D36 |
Penetration at 25o C | 20-30 dmm | ASTM D5 |
Cold Flexibility 0o C | No cracking | ASTM D 412 |
Tensile Strength(N/5 cm) | - | ASTM D 412 |
Longitudinal | 650 | - |
Transverse | 450 | - |
Elongation at break(%) | - | ASTMD 412 |
Longitudinal Min | 45 | ASTMD 5147 |
Transverse | 50 | - |
Features : LDO comprises blend of MFO with distillate fuel with small proportion of residual fuel This Fuel Oil density starts from 0.85 to 0.91.
Specifications : Developed as per industry specifications Used as fuel for lower RPM engines Also used as fuel for lift irrigation pump sets, DG sets, boilers and furnaces and specialized for Hotmix Plant.
Uses of Light Diesel Oil (LDO) :
Physical characteristics of jai outer wrap as per awwa-c-203-1991 are as follows :
Specification
Characteristics | Unit | Requirement |
---|---|---|
Nominal thickness | mm | 0.75 |
Mass | g/m2 | 550 |
Breaking Strength | N/150 mm of width, Min | 535 |
Tear strength (Transverse) | N/Min | 45 |
Inner diameter of core | mm | 63 to 75 |
Mass | g/m2, Min | 40 |
Thickness | mm, Min | 0.33 |
Breaking strength | N/cm, Min | 23.2 |
Tear strength | N, Min | 9 |
Porosity | The inner wrap shall have a porosity, when related to pressure difference across the sample of not less than 0.55 mm & not more than 1.9 mm of water guage, at an air velocity of 1 m/s. | - |
Temperature resistance | Unaffected under load in hot bitumen at 288o C for 1 minute | - |
Pliability | There shall be no cracking when bent over a 3 mm radius, after immersing in water for 10-15 minutes through a 90° arc. | - |
JAI RBA Compound (C P R X) is a cold applied rubberised bituminous adhesive in the form of an emulsion of brushable consistency.
Recommended Uses :
Surface Preparation : The surface should be free from dust, grease rust and loose particles.
Instruction : Stir well before use.
Specification
Characteristic | Requirements |
---|---|
Form And Conditions | Homogenous, Thixotropic. |
Consistency | Smooth And Uniform For Brushing. |
Mass In Kg Per Ltr. | 1+0.09 |
Initial Set | 4-6 Hrs. |
Curring Time (Min.) | 24 Hrs. |
Ph Value Of Emulsion | 8.0 To 9.5 |
Coverage | 1.5 To 1.75 Ltrs./sq.mtr. Per Coat |
Total Non-Volatile Matter | - |
Solid By % Age (Min.) | 50 |
Ash Content (Max.) | 0.02 |
Solvent For Removal | - |
Wet | Water |
Dry | Kerosene / Solvent |
We are capable of handling both automated inbound and outbound consignments, we have excellent warehousing solutions available. We keep the extensive array of products sorted to make sure that the delivery commences thoroughly. Be it packaging small or large consignments, light or heavy products, we use the finest material to provide cost efficient and sustainable packaging solutions.