| Brand | Aws | Deposited Metal | Chemical Composition | ||||||||||
| Cu | Mn | Si | S | P | Zi | Ti | Cr | Mo | |||||
| Tensile Strength MPA | Yield | Elongation | |||||||||||
| WT72 | ER 70S-2 | 480 | 400 Min.. | 24 Min. | 0.07 max | 0.90 -1.40 | 0.40- 0.70 | 0.030 max | 0.03 | 0.02 -0.70 | 0.05 -0.10 | - | - |
| WT80 | ER 80S-B2 | 635 | 520 Min. | 25 Min. | 0.12 | 0.40 -0.70 | 0.7 | 0.03 | 0.03 | - | - | 1.20 -1.50 | 0.40- 0.60 |
Technical Specifications
| Brand | Aws | Chemical Composition | ||||||||
| Cu | Si | Fe | Mn | Mg | Cr | Zn | Ti | AL | ||
| WT-1100 | ER-1100 | 0.05-0.20 | 10 | - | 0.05 | - | - | 0.1 | - | 99.5 |
| WT-4043 | ER-4043 | 0.3 | 4.5-6.0 | 0.8 | 0.05 | 0.05 | - | 0.1 | 0.2 | Rem |
Technical Specifications
| Brand | Aws | Chemical Composition | ||||||||
| Cu | Si | Fe | Mn | Mg | Cr | Zn | Ti | AL | ||
| WT-1100 | ER-1100 | 0.05-0.20 | 10 | - | 0.05 | - | - | 0.1 | - | 99.5 |
| WT-4043 | ER-4043 | 0.3 | 4.5-6.0 | 0.8 | 0.05 | 0.05 | - | 0.1 | 0.2 | Rem |
Technical Specifications
| Brand | Aws | Deposited Metal | Chemical Composition | ||||||||||
| Cu | Mn | Si | S | P | Zi | Ti | Cr | Mo | |||||
| Tensile Strength MPA | Yield | Elongation | |||||||||||
| WT72 | ER 70S-2 | 480 | 400 Min.. | 24 Min. | 0.07 max | 0.90 -1.40 | 0.40- 0.70 | 0.030 max | 0.03 | 0.02 -0.70 | 0.05 -0.10 | - | - |
| WT80 | ER 80S-B2 | 635 | 520 Min. | 25 Min. | 0.12 | 0.40 -0.70 | 0.7 | 0.03 | 0.03 | - | - | 1.20 -1.50 | 0.40- 0.60 |
Technical Specifications
| Brand | AWS | Deposited Metal | Chemical Composition | ||||||
| Tensile Strength Mpa | Elongation (%) | C | Mn | Si | Cr | Ni | Mo | ||
| WT 304L | ER 304L | 597 | 43 | 0.03 | 1.27 | 0.51 | 18.3 | 9.4 | - |
| WT308L | ER 308L | 578 | 42 | 0.02 | 1.65 | 0.42 | 20.1 | 10.33 | - |
| WT 309L | ER 309L | 588 | 43 | 0.02 | 1.98 | 0.39 | 23.88 | 12.9 | - |
| WT 310 | ER 310 | 607 | 41 | 0.09 | 2.01 | 0.4 | 27.4 | 21.8 | - |
| WT 316L | ER 316L | 558 | 40 | 0.03 | 1.91 | 0.42 | 19.1 | 12.58 | 2.57 |
| WT 410 | ER 410 | 510 | 25 | 0.1 | 0.43 | 0.54 | 11.81 | 0.17 | - |
| WT 430 | ER 430 | 468 | 36 | 0.04 | 0.46 | 0.39 | 16.37 | 0.2 | - |
Characteristics :-
Classifications :-
Wire Composition
| C | Mn | Si | S | P | Cu |
|---|---|---|---|---|---|
| 0.06-0.15 | 1.40-1.85 | 0.80-1.15 | 0.035 Max | 0.025 Max | 0.50 Max |
All Weld Mechanical Properties ( Under Co2 Shield And Normal Welding Condition )
| YS (N/MM') | U.T.S (N/MM') | Elong (GL = 4D) | Charpy-V Impact Values At |
|---|---|---|---|
| 400 Min. | 480 Min. | 22% Min. | -29 c> 27j |
Packing Specification
| Dimension | Weight | Packing Boxes |
|---|---|---|
| 300mm x 52mm x 100mm | 13.5 Kg Approx | supplied all plastic spools,sealed in polythin bags and packed shrink wrapped comugated boxes |
Technical Specification
| Brand | AWS | Deposited Metal | Chemical Composition | ||||||
| Tensile Strength Mpa | Elongation (%) | C | Mn | Si | Cr | Ni | Mo | ||
| WT 304L | ER 304L | 597 | 43 | 0.03 | 1.27 | 0.51 | 18.3 | 9.4 | - |
| WT308L | ER 308L | 578 | 42 | 0.02 | 1.65 | 0.42 | 20.1 | 10.33 | - |
| WT 309L | ER 309L | 588 | 43 | 0.02 | 1.98 | 0.39 | 23.88 | 12.9 | - |
| WT 310 | ER 310 | 607 | 41 | 0.09 | 2.01 | 0.4 | 27.4 | 21.8 | - |
| WT 316L | ER 316L | 558 | 40 | 0.03 | 1.91 | 0.42 | 19.1 | 12.58 | 2.57 |
| WT 410 | ER 410 | 510 | 25 | 0.1 | 0.43 | 0.54 | 11.81 | 0.17 | - |
| WT 430 | ER 430 | 468 | 36 | 0.04 | 0.46 | 0.39 | 16.37 | 0.2 | - |
Technical Specifications
| Brand | AWS | Deposited Metal | Chemical Composition | ||||||
| Tensile Strength Mpa | Yield | Bongation (%) | C | Mn | Si | S | P | ||
| WT-08 | EL-8 | 510-610 | 400 Min. | 22 Min. | 0.1 | 0.25-0.60 | 0.07 | 0.03 | 0.03 |
| WT-12K | El-12K | 410-550 | 320 Min. | 22 Min. | 0.1 | 0.80-1.10 | 0.07 | 0.03 | 0.03 |