The Hot Face Insulation Bricks are manufactured by us is fabricated using finest quality raw material. The Hot Face Insulation Bricks are widely used in various industries to provide insulation from hot temperatures. With high tensile strength, efficient performance the Hot Face Insulation Bricks has been widely appreciated by the customers.
Specifications
Type | RR500 | RR600 | RR700 | RRCF | RRHF | RRHFI | RRHER | RRHS | RRSI |
---|---|---|---|---|---|---|---|---|---|
B.D. (Gm/cc) Max. | 0.53 | 0.63 | 0.7 | 0.8 | 0.9 | 1 | 1.1 | 1.2 | 1 |
CCS(Kg /cm2) Min. | 7 | 9 | 12 | 15 | 20 | 40 | 40 | 80 | 15 |
A.P. (%) Min. | 80 | 75 | 72 | 70 | 65 | 60 | 55 | 55 | 65 |
T.C. at 600oHF Temp. Kcal/m/hr/oC) Max. | 0.14 | 0.16 | 0.18 | 0.19 | 0.25 | 0.3 | 0.4 | 0.4 | 0.25 |
PLC (%) for 5 hrs., Max. | 1.5 at 950oC | 1.5 at 1000oC | 1.5 at 1000oC | 1.5 at 1000oC | 2.0 at 1000oC | 1.5 at 1200oC | 1.5 at 1250oC | 1.5 at 1200oC | 1.5 at 1100oC |
SWT (oC) Min. | 1000 | 1000 | 1050 | 1050 | 1100 | 1200 | 1300 | 1350 | 1150 |
PCE (OC) Min. | - | - | - | - | 27 | 30 | 32 | 30 | - |
Al2O3 (%) Min. | - | - | - | 28 | 30 | 35 | 40 | 18 | 18 |
CiO2 (%) Min. | - | - | - | 60 | 62 | 60 | 50 | 70 | 75 |
Fe2O3 (%) Max. | - | - | - | 2 | 2 | 2 | 2 | 2 | 2 |
Composition
Properties | Unit | RRHF |
---|---|---|
Bulk Density (B.D.) | Gm/cm3 | 0.90 (Max) |
Cold Crushing Strength (CCS) | Kg/cm2 | 20.0 (Min) |
Apparent Porosity (AP) | % | 65 (Min) |
TC at 600 Deg C HF Temp. | Kcal/m/hr/Deg C | 0.25 (Max) |
PLC for 5 hours @ 1000 Deg C | % | +/- 1.5 (Max) |
SWT | Deg C | 1100 (Max) |
We are among the prime Manufacturers, Suppliers, Importers and Exporters of Mica Insulation Bricks. Meticulously designed, the Mica Insulation Bricks are in great demand in the national and international market. Our range of Refractory Bricks is manufactured in accordance with set industrial standards.
Specifications
Type | RR500 | RR600 | RR700 |
---|---|---|---|
B.D. (Gm/cc) Max. | 0.53 | 0.63 | 0.7 |
CCS (Kg/cm2) Min. | 7 | 9 | 12 |
A.P. (%) Min. | 80 | 75 | 72 |
T.C. at 600oHF Temp. (Kcal/m/hr/oC) Max.. | 0.14 | 0.16 | 0.18 |
PLC (%) for 5 hrs. Max. | 1.5 at 950oC | 1.5 at 1000oC | 1.5 at 1000oC |
SWT (oC) Max. | 1000 | 1000 | 1050 |
Composition
Properties | Unit | RR500 | RR600 | RR700 |
---|---|---|---|---|
Bulk Density (B.D.) | Gm/cm3 | 0.53 (Max) | 0.62 (Max) | 0.70 (Max) |
Cold Crushing Strength (CCS) | Kg/cm2 | 7.0 (Min) | 9.0 (Min) | 10.0 (Min) |
Apparent Porosity (AP) | % | 80 (Min) | 75 (Min) | 72 (Min) |
TC at 600 Deg C HF Temp. | Kcal/m/hr/Deg C | 0.14 (Max) | 0.16 (Max) | 0.18 (Max) |
PLC for 5 hours | % | +/- 1.5 (Max) @ 950 Deg C | +/- 1.5 (Max) @ 1000 Deg C | +/- 1.5 (Max) @ 1000 Deg C |
SWT | Deg C | 950 (Max) | 1000 (Max) | 1050 (Max) |
We are among the foremost Manufacturers, Suppliers, Importers and Exporters of the Cold Face Insulation Bricks. The Cold Face Insulation Bricks offered by is manufactured with precision by our experts. Fabricated using high grade material the Insulation Bricks are in compliance with international standards. Moreover, the wide range of Cold Face Insulation Bricks is available in the market at reasonable prices.
Features
Specifications
Type | RRCF | RRHF |
---|---|---|
B.D. (G.m/cc) Max. | 0.8 | 0.9 |
CCS (Kg/cm2) Min. | 15 | 20 |
A.P. (%) | 70 | 65 |
T.C.at 600oF Temp. (Kcal/m/hr/oC) Max. | 0.19 | 0.25 |
PLC (%) for 5 hrs., Max. | 1.5 at 1000oC | 2.0 at 1000oC |
SWT (C) Max. | 1050 | 1100 |
PCE (OC) Min. | - | 27 |
Al2O3 (%) Min. | 28 | 30 |
SiO2(%) Min. | 60 | 62 |
Fe2O3 (%) Max. | 2 | 2 |
Composition
Properties | Unit | RRCF |
---|---|---|
Bulk Density (B.D.) | Gm/cm3 | 0.85 (Max) |
Cold Crushing Strength (CCS) | Kg/cm2 | 15.0 (Min) |
Apparent Porosity (AP) | % | 70 (Min) |
TC at 600 Deg C HF Temp. | Kcal/m/hr/Deg C | 0.19 (Max) |
PLC for 5 hours @ 1000 Deg C | % | +/- 1.5 (Max) |
SWT | Deg C | 1050 (Max) |
We are among the foremost Manufacturers, Suppliers, Importer and Exporter of superior quality Kyanite Insulation Bricks. Meticulously designed, these Kyanite Insulation Bricks have been demanded widely in national and international market. Owing to its unique features like high strength, durability it has been widely appreciated in the market.
Specifications
Type | RRHFK |
---|---|
B.D. (Gm/cc) Max. | 1.1 |
CCS (Kg/cm2) Min. | 40 |
A.P. (%) Min. | 55 |
T.C. at 600oHF Temp. (Kcal/m/hr/oC) Max. | 0.4 |
PLC (%) for 5 hrs. Max. | 1.5 at 1250oC |
SWT (oC) Max. | 1300 |
PCE (OC) Min. | 32 |
Al2O3 (%) Min. | 40 |
SiO2(%) Min. | 50 |
Fe2O3 (%) Max. | 2 |
Composition
Properties | Unit | RRHFK |
---|---|---|
Bulk Density (B.D.) | Gm/cm3 | 1.10 (Max) |
Cold Crushing Strength (CCS) | Kg/cm2 | 35.0 (Min) |
Apparent Porosity (AP) | % | 55 (Min) |
TC at 600 Deg C HF Temp. | Kcal/m/hr/Deg C | 0.40 (Max) |
PLC for 5 hours @ 1250 Deg C | % | +/- 1.5 (Max) |
SWT | Deg C | 1300 (Max) |
PEC | OC | 29 (Min) |
Al2O3 | % | 40 (Min) |
SiO2 | % | 50 (Min) |
Fe2O3 | % | 2 (Max) |
The Light Weight Insulation Bricks manufactured by us are highly demanded across the globe owing to superior quality. Fabricated using high grade material, the Light Weight Insulation Bricks is well- known in the market for their durability, accurate dimensions and reliability.
Specifications
Type | RRHFK |
---|---|
B.D. (Gm/cc) Max. | 1 |
CCS (Kg/cm2) Min. | 40 |
A.P. (%) Min. | 60 |
T.C. at 600oHF Temp. (Kcal/m/hr/oC) Max. | 0.3 |
PLC (%) for 5 hrs. Max. | 1.5 at 1200oC |
SWT (oC) Max. | 1200 |
PCE (OC) Min. | 30 |
Al2O3 (%) Min. | 35 |
SiO2(%) Min. | 60 |
Fe2O3 (%) Max. | 2 |
The Silica Insulation Bricks manufactured by us has been in huge demand in national and international market. Owing to its unique features like durability, high quality, and light weight, our Silica Insulation Bricks has been widely appreciated by the customers. Moreover, we are also engaged in providing customized range of Silica Insulation Bricks.
Features
Specifications
Type | RRHS | RRSIB |
---|---|---|
B.D. (Gm/cc) Max. | 1.2 | 1 |
CCS (Kg/cm2) Min. | 80 | 15 |
A.P. (%) Min. | 55 | 65 |
T.C.at 600oHF Temp. (Kcal/m/hr/oC) Max. | 0.4 | 0.25 |
PLC (%) for 5 hrs., Max. | 1.5 at 1200oC | 1.5 at 1100oC |
SWT (oC) Max. | 1350 | 1150 |
PCE (OC) Min. | 30 | - |
Al2O3 (%) Min. | 18 | 18 |
SiO2(%) Min. | 70 | 75 |
Fe2O3 (%) Max. | 2 | 2 |
Composition
PROPERTIES | Unit | RRHS | RRSIB |
---|---|---|---|
Bulk Density (B.D.) | Gm/cm3 | 1.10 (Max) | 1.00 (Max) |
Cold Crushing Strength (CCS) | Kg/cm2 | 80 (Min) | 25 (Min) |
Apparent Porosity (AP) | % | 55 (Min) | 60 (Min) |
TC at 600 Deg C HF Temp. | Kcal/m/hr/Deg C | 0.25 (Max) | 0.40 (Max) |
PLC for 5 hours | % | +/- 1.5 (Max) @ 1200 Deg C | +/- 1.5 (Max) @ 1100 Deg C |
SWT | Deg C | 1350 (Max) | 1150 (Max) |
PEC | OC | 30 (Min) | - |
Al2O3 | % | 18 (Min) | 20 (Min) |
SiO2 | % | 75 (Min) | - |
Fe2O3 | % | 2 (Max) | 2 (Max) |