1 Products availableWe are leaders in the market for providing best range of Magnesia Bricks, Acid Resistant Bricks, Silicon Carbide Bricks, fireclay alumina bricks and chrome bricks
Details
Product | MgO % | CaO % | SiO2 % | Fe2O3 % | Al2O3 % | A.P % | CCS kg/cm2 | RUL (Ta)OC Max | Application |
---|---|---|---|---|---|---|---|---|---|
CC-MGR | 87 | 2 | 6.5 | - | 1 | 22 | 350 | 1550 | EAF, LD & Ladle Backup |
CC-MGD | 92 | 2 | 4 | - | 0.8 | 18 | 600 | 1600 | Hot Metal Mixer |
CC-M-96 | 96 | 2 | 1 | 0.5 | 0.3 | 17 | 500 | 1700 | Glass Tank Regenerator |
Our entire range is value for money, as it is quality guaranteed, sold after a string of quality control tests, and is relied on by many. By making use of quality packing material, we are able to ensure that the orders will remain free from damage during transit. Also, our expert packing personnel strictly check the entire lot before final dispatch.
Details
Properties | Unit | Class-I Bricks | Class-II Bricks | Application |
---|---|---|---|---|
Water Absorption | % Max | 2 | 4 | Chemical Process Floor, Chimneys, Tanks etc. |
Flexural Strenght | Kg/cm2 | 100 | 70 | |
Compressive Strength | Kg/cm2 | 700 | 500 | |
Resistance to Acid | Loss in weight % Max | 1.5 | 4 |
Details
Product | SiC % | Al2O3 % | Fe2O3 % | B.D* (gm/cc) | A.P.* % | CCS (kg/cm2) | HMOR at 1350oC (kg/cm) | Thermal Conductivity 1000oC W/mk | RUL oC | Application Area |
---|---|---|---|---|---|---|---|---|---|---|
CC-SiC | 83 | 2 | 1 | 2.5 | 16 | 700 | 175 | 14.7 | 1720 | Posts in Kiln cars, shape for Ferro alloy industry |
Note :
Details
Product | Al2O3% | Fe2O3% | A.P% | B.D gm/cc | CCS Kg/cm2 | PLC % | PCE(SK) | RUL(Ta)oC | Application Area |
---|---|---|---|---|---|---|---|---|---|
CC-BS(B) | 36 | 1.7 | 18 | 2.15 | 300 | ±0.30 at 1450oC/2 hrs | 31 | 1450 | Blast Furnace Stack Lining |
CC-42D | 42 | 1.5 | 16 | 2.25 | 400 | ±0.5 at 1450oC/2 hrs | 33 | 1500 | Blast Furnace Lining |
CC-45 | 45 | 1.5 | 21 | 2.2 | 350 | ±0.50 at 1500oC/2 hrs | 34 | 1450 | Blast Furnace Lining, Cement Rotary Kiln, Lime Calcination Kiln, Glass Tank Furnace |
CC-45D | 45 | 1.5 | 16 | 2.3 | 450 | ±0.30 at 1450oC/2 hrs | 34 | 1500 | Blast Furnace Lining, Cement Rotary Kiln, Lime Calcination Kiln, Glass Tank Furnace |
CC-CB | 50 | 1.3 | 18 | 2.35 | 350 | ±0.30 at 1500oC/2 hrs | 34 | 1530 | Anode baking furnace |
CC-CHL | 50 | 1.5 | 9 | 2.42 | 700 | - | - | 1550 | Chlorinator |
CC-55D | 55 | 1.5 | 18 | 2.4 | 500 | ±0.50< at 1450oC/2 hrs | 35 | 1520 | Blast Furnace Lining, Cement Rotary Kiln, Lime Calcination Kiln, Glass Tank Furnace |
CC-HIAL59 | 59 | 1.2 | 18 | 2.5 | 500 | ±0.50 at 1450oC/2 hrs | 36 | 1600 | BF hot blast main, Glass tank furnace |
CC-HIAL 50 | 50 | 1.1 | 18 | 2.4 | 400 | ±0.5 at 1450oC/4 hrs | 34 | 1520 | Anode baking furnace |
CC-AL65-SIC | 65 | 1.5 | 12 | 2.65 | 400 | - | 36 | 1650 | Torpedo Ladel |
CC 45B | 45 | 3.5 | 22 | 2.25 | 300 | ±1.5 at 1350oC/2 hrs | 33 | 1350 | Cement Plants |
CC 50B | 50 | 3.5 | 22 | 2.3 | 350 | ±1.5 at 1400oC/2 hrs | 33 | 1370 | Cement Plants |
CC-60B LF | 60 | 2.5 | 22 | 2.45 | 450 | ±2.0 at 1450oC/2 hrs | 35 | 1420 | - |
CC-60B | 60 | 3 | 22 | 2.4 | 400 | ±2.0 at 1450oC/2 hrs | 34 | 1400 | - |
CC-62 | 62 | 1.5 | 22 | 2.4 | 350 | ±0.40 at 1500oC/2 hrs | 36 | 1500 | Blast Furnace Stove Checkers, BF lining |
CC-62D | 62 | 1.2 | 16 | 2.5 | 600 | ±0.20 at 1500oC/2hrs | 36 | 1550 | Blast Furnace Hearth & tuyere |
CC-HIAL 62 | 62 | 1.2 | 18 | 2.52 | 500 | ±0.3 at 1500oC/2hrs | 36 | 1600 | Blast furnace checkers |
CC-70 | 70 | 1.5 | 20 | 2.6 | 500 | ±0.3 at 1500oC/2hrs | 36 | 1550 | Rotary kiln Lining |
CC-Mul-70 | 70 | 0.8 | 20 | 2.5 | 500 | ±0.20 at 1550oC/2hrs | 36 | 1700 | Blast Furnace Hearth & Tap hole, Glass Tank Furnace |
CC-Mul-70(F) | 70 | 0.5 | 17 | 2.55 | 600 | ±0.20 at 1550oC/2hrs | 36 | 1720 | Blast Furnace Hearth & Tap hole, Glass Tank Furnace |
CC-70B (LF) | 70 | 2.5 | 20 | 2.6 | 500 | ±3.0 at 1600oC/2hrs | 36 | 1480 | EAF Roof, Ladle |
CC-70B | 70 | 3 | 22 | 2.55 | 450 | ±3.0 at 1450oC/2hrs | 35 | 1440 | EAF Roof |
CC-80B (LF) | 80 | 2.5 | 20 | 2.7 | 500 | ±3.0 at 1600oC/2hrs | 37 | 1500 | EAF Roof |
CC-80B | 80 | 3 | 22 | 2.7 | 500 | ±3.0 at 1600oC/2hrs | 35 | 1460 | EAF Roof |
CC-85CBC | 84 | 1.5 | 20 | 2.7 | 700 | ±0.5 at 1500oC/2hrs | 37 | 1580 | Aluminium Melting & Holding Furnace |
CC-85DG | 85 | 1.5 | 20 | 2.9 | 500 | ±0.5 at 1500oC/2hrs | 37 | 1650 | Torpedo Ladle lining |
CC-88X | 88 | 2 | 18 | 2.85 | 800 | ±0.5 at 1500oC/2hrs | 37 | 1580 | Reheating furnace hearth |
CC-90XD | 90 | 0.5 | 18 | 2.92 | 600 | ±0.2 at 1500oC/2hrs | 38 | 1700 | Carbon black reactor |
CC-95 | 95 | 0.5 | 22 | 3 | 600 | ±0.2 at 1500oC/2hrs | 38 | 1700 | Secondary Steel making Vessel, chemical, petrochemical & Fertilizer application |
Details
Product | MgO % | Cr2O3 % | SiO2 % | A.P % | CCS kg/cm2 | RUL (Ta)OC Max | Application |
---|---|---|---|---|---|---|---|
CC-MGR | 63 | 11 | 6.3 | 22 | 300 | 1600 | Open Hearth Roof |
CC-MC40S3 | 60 | 15 | 3 | 20 | 300 | 1700 | Rotary Kiln for dead Buring Dolomite |
CC-CMN | 35 | 22 | - | 22 | 250 | 1600 | Backup Lining |
Details
Product | MgO % | Cr2O3 % | SiO2 % | A.P % | B.D gm/cc | CCS kg/cm2 | RUL (Ta)OC | Application |
---|---|---|---|---|---|---|---|---|
CC-CR-VX | 58 | 20 | 0.8 | 18 | 3.15 | 400 | 1720 | Copper,Glass, VOD & Zinc Furnaces |
CC-CR-VV | 60 | 18 | 1.5 | 18 | 3 | 400 | 1700 | Copper,Glass, VOD & Zinc Furnaces |
CC-CR-XV | 55 | 24 | 1 | 17 | 3.18 | 550 | 1750 | Copper smelting & converting Furnaces |
CC-RH | 58 | 18 | 1 | 18 | 3.15 | 400 | 1700 | Snorkel & Lower vessel of RH degasser |
Details
Product | MgO % | F.C % | A.P % | B.D gm/cc | CCS kg/cm2 | HMOR kg/cm2 | Application |
---|---|---|---|---|---|---|---|
CC-HMR-LD | 97 | 8 | 5 | 3 | 300 | 90 | LD Convertor Bottom & Tap Pad |
CC-HMR-SL | 97 | 10 | 5 | 3 | 300 | - | Steel Ladle |
Details
Product | Al2O3 % | MgO % | F.C % | A.P % | B.D gm/cc | CCS kg/cm2 | Application |
---|---|---|---|---|---|---|---|
CC-AMC-1 | 70 | 8 | 5 | 6 | 2.8 | 400 | Steel Ladle Bottom & Metal Zone |
CC-AMC-3 | 80 | 8 | 5 | 5 | 3.1 | 400 | Steel Ladle Bottom & Metal Zone |
We source the raw material from the trusted places in the market. As a result of which, the finished products stand high on the expectations of the clients. Looking for trusted Non Recovery Coke Oven Bricks suppliers? We are the perfect ones and capable of fulfilling bulk orders.
Grading : 95% min. will pass through maximum grain size indicated.
Details
Products | Al2O3 % |
Fe2O3 % |
A.P % |
CCS Kg/CM2 |
PLC % |
RUL (Ta) ®C |
PCE (®C) |
---|---|---|---|---|---|---|---|
CC-NRC-(40) | 38 | 2 | 24 | 250 | +0.1 -0.5 |
1350 | 1740 |
CC-NRC-(50) | 48 | 1.5 | 22 | 400 | +0.1 -0.4 |
1420 | 1750 |
CC-NRC-(55) | 55 | 1.5 | 22 | 450 | +0.1 -0.4 (1500®C/2 hrs) |
1470 | 1770 |
CC-NRC-(65) | 65 | 1.5 | 23 | 500 | +0.1 -0.4 (1500®C/2 hrs) |
1500 | 1790 |
Details
Product | ZrO2 % | Al2O3 % | B.D* (gm/cc) | A.P.* % | CCS (kg/cm2) | RUL oC | Application Area |
---|---|---|---|---|---|---|---|
CC-ZR | 62 | - | 3.3 | 20 | 500 | 1600 | For Bottom paving & other locations of Glass Tank Furnace |
CC-ZMG | 18 | 68 | 3.1 | 21 | 500 | 1650 | For Bottom paving & other locations of Glass Tank Furnace |