As we want to maintain transparency in the business dealings, we offer an invoice stating all the necessary details of the payment and also ensure that the transactions should remain safe. Being a quality-conscious firm, we are offering nothing short of the best quality products from Shanghai(China). Square Carbon Cup for CE-Meter (Carbon and Silicon Analyzer)

Application : The square expendable carbon cup is for determining the Carbon equivalent, % Carbon and % Silicon in molten iron by using the principle of thermal analysis.

Features :

• International standard specification.
• Japan-imported couple wire.
• High accuracy, rapid reaction, reliability, stability, smooth cooling curve and good reproductivity.
• Sold to Japan, Korea, Thailand, Malaysia, Taiwan etc.
• Determination of thermal stability of sample cup And Instrument
• Adjustment One -  option of instrument and electric furnace Be sure to select the specific carbon silicon analyzer and hot metal within the specified test furnace. the replacement of components when the next test furnace hot metal will be change.
• Two - data testing methods  Example - Thermal analysis of the test sample cup should be 3 to 5 consecutive (arrange it according the time), e.g. the test result of Si% is 1.80%, 1.82%, 1.86%, 1.88%, 1.90%. Testing is completed record data.
• Three - analysis Stability. According above testing result, the highest one is 1.80%, lowest one is 1.70%, fluctuation gap is 0.1, average value is 1.75% (±0.05). Instrument adjustment. If the chemical analysis of Si% molten iron content was 1.85% when the original apparatus should be set based on the si values of 0.1 and then raised to complete the adjustment (if the former setting of Si is -0, 2, should change at -0.1). when test again, the content of Si% will become 1.85%, the adjustment is over, can work now.
• Four - attention the hot metal temperature in the sample cup should not exceed 1350.
• Optimum temperature of ductile iron is 1200 1250.
• Optimum temperature of Gray Iron 250, 300 is 1250   1350
• The abnormal situation like low carbon high silicon hot metal composition will cause instruments to measure the normal C% and Si% no data.

Stationed in Shanghai(China), our organization is one of the prime most providers in the industry today. We make sure that the products we offer to our clients will remain free from any kind of damage. Thus, we store the entire lot under secured environment in our capacious warehouse.

Details :

• Carbon Equivalent Meter Cup (Thermal Analysis Cup) for Casting Industry Analysis Thermal Analysis cup composition
• Resin bonded sand - Sand (SiO2 >94% and Silt content < 0.3%) - Thermoplastic phenol resin 6-10% of sand - Urotropine (resin hardener) 10-15% of resin
• Tellurium grains
• Silica coating
• K- type thermocouple tube Production Well-graded and clean sand, thermoplastic phenol resin and Urotropine (resin hardener) are dry mixed at the temperature of 500 degree Celsius to produce  resin bonded sand . This resin bonded sand is shot into the pre-heated mold with having the K-type thermocouple tube inside.
• At the temperature of 250degree Celsius, the cup is formed by the resin bond. This cup is coated inside with silica for being thermal insulation and then filled in the cup with 15 gram of Tellurium. By means of drying this coated cup at the temperature of 80 degree Celsius for 4 hours, the carbon cup is ready for the casting control.

Application : The expendable carbon cup (thermal analysis cup) is for determining the Carbon equivalent, % Carbon and % Silicon in molten iron by using the principle of thermal analysis.

The advantages of this carbon cup are as follows :

• With Tellurium grain, the complete white iron solidification can be met
• Fast thermocouple response
• Precisely measuring the temperature of melting iron sample
• Provide uniform cooling curve
• High accuracy of the content of Carbon and Silicon
• Improve the casting process control

SPG-cup for Stove-front Molten Iron Quality Management Meter same like carbon cup, but without tellurium coating inside. test the molten iron nodularity (rate of spheroidization) for stove-front molten iron quality management meter.