Square Carbon Cup

As we want to maintain transparency in the business dealings, we offer an invoice stating all the necessary details of the payment and also ensure that the transactions should remain safe. Being a quality-conscious firm, we are offering nothing short of the best quality products from Shanghai(China). Square Carbon Cup for CE-Meter (Carbon and Silicon Analyzer)
Application : The square expendable carbon cup is for determining the Carbon equivalent, % Carbon and % Silicon in molten iron by using the principle of thermal analysis.
Features :

• International standard specification.
• Japan-imported couple wire.
• High accuracy, rapid reaction, reliability, stability, smooth cooling curve and good reproductivity.
• Sold to Japan, Korea, Thailand, Malaysia, Taiwan etc.
• Determination of thermal stability of sample cup And Instrument
• Adjustment One -  option of instrument and electric furnace Be sure to select the specific carbon silicon analyzer and hot metal within the specified test furnace. the replacement of components when the next test furnace hot metal will be change.
• Two - data testing methods  Example - Thermal analysis of the test sample cup should be 3 to 5 consecutive (arrange it according the time), e.g. the test result of Si% is 1.80%, 1.82%, 1.86%, 1.88%, 1.90%. Testing is completed record data.
• Three - analysis Stability. According above testing result, the highest one is 1.80%, lowest one is 1.70%, fluctuation gap is 0.1, average value is 1.75% (±0.05). Instrument adjustment. If the chemical analysis of Si% molten iron content was 1.85% when the original apparatus should be set based on the si values of 0.1 and then raised to complete the adjustment (if the former setting of Si is -0,2, should change at -0.1). when test again, the content of Si% will become 1.85%, the adjustment is over, can work now.
• Four - attention the hot metal temperature in the sample cup should not exceed 1350.
• Optimum temperature of ductile iron is 1200 ~ 1250.
• Optimum temperature of Gray Iron 250, 300 is 1250   ~ 1350
• The abnormal situation like low carbon high silicon hot metal composition will cause instruments to measure the normal C% and Si% no data.