Laiwu Taishan Sunlight Welding Materials Co. ltd

Laiwu, Shandong Pr. China, China

We are offering welding flux (sj501). Ty.sj501 equivalent to lincoln 780 welding flux quality system: iso9001:2008certification: abs specification: en760 sa ar 1 88 ac h5 aws a5.17 f7a0-el12 f7a2-em12k applications:butt and flat fillet welding of miniature lpg tanks, ships, vehicles, agricultural implements, machinery, boilers, pressure vessles, bridges, structural steels. characteristics: 1.ty-sj501 is an agglomerated aluminate- rutile type flux. 2. Metallurgical behavior: high silicon and manganese pick- up is obtained. 3. Grain size: 14 to 60 mesh.basicity: 0.7( biiw). 4. The welding performance is excellent. Slag detachability is very good, especially at high speed.Welding porosity scarcely occur. 5. Its welding speed can travel up to 120 cm min. It is particularly useful for welding tube- web- tube joints of finned tubes. 6.ty-sj501 is useful for welding thin plate in single pass and limited pass. 7.the flux has low moisture pick-up and granular stability . As the bulk density is low so is the consumption rate. Caution:1.damp flux should be re-dried at 300-350 centigrade for 2 hours.2.rust, grease and moisture on the weldment should be removed before welding. chemical composition of sj501 sio2+tio2caf2ai2o3+mnocao s p25-35 5-10 50-60 3-100.050.05 chemical composition of deposited metal wire c si mnem12k0.05- 0.100.05- 0.10 1.4- 1.6 standard package: kraft bag with anti-moisture plastic lining inside. 25kgbag, 40bagsplywood pallet, 24 pallets in 20'gp container, size:24 cbm ty.sj501 for lpg cylinder weldingsmooth welding bead, excellent slag detachability !

We are offering welding flux . Flux sj501 equivalent to lincoln 780 welding flux quality system: iso9001:2008certification: abs specification: en760 sa ar 1 88 ac h5 aws a5.17 f7a0-el12 f7a2-em12k applications:butt and flat fillet welding of miniature lpg tanks, ships, vehicles, agricultural implements, machinery, boilers, pressure vessles, bridges, structural steels. characteristics: 1.ty-sj501 is an agglomerated aluminate- rutile type flux. 2. Metallurgical behavior: high silicon and manganese pick- up is obtained. 3. Grain size: 14 to 60 mesh.basicity: 0.7( biiw). 4. The welding performance is excellent. Slag detachability is very good, especially at high speed.Welding porosity scarcely occur. 5. Its welding speed can travel up to 120 cm min. It is particularly useful for welding tube- web- tube joints of finned tubes. 6.ty-sj501 is useful for welding thin plate in single pass and limited pass. 7.the flux has low moisture pick-up and granular stability . As the bulk density is low so is the consumption rate. Caution:1.damp flux should be re-dried at 300-350 centigrade for 2 hours.2.rust, grease and moisture on the weldment should be removed before welding. chemical composition of sj501 sio2+tio2 caf2 ai2o3+mno cao s p25-35 5-10 50-60 3-10 0.05 0.05 chemical composition of deposited metal wire c si mnem12k 0.05- 0.10 0.05- 0.10 1.4- 1.6 wire standard yield point s(mpa) tensile strengthb(mpa) elongation 5(%) impact valueakv el12 f7a0-el12 330 420 22 53 (-18c)em12k f7a2-em12k 410

We are offering welding flux . Soldering flux ty.sj101 specifications: aws a5.17 f7a2-em12k f7a4-eh14certification: abs ccs applications: single and multi-layer welding of 1.api pipes(x52, x60, x70, x80 grade steels)2.thick-wallstructures of different kinds of high-tensile strength steel characteristics: 1.ty.sj101g is an agglomerated fluoride-basic type flux 2. Metallurgical behavior: the behavior of silicon and manganese is neutral, so it is better to weld with wires containing relatively high manganese and silicon. 3. Basicity: 3.1(biiw) 4. As a result of low hydrogen levels(max.5ml100g), low oxygen, sulfur, phosphor levels in the all weld deposites, unform mechanical properties with low temperature toughness are obtained. 5.slag is extremely easy to remove and bead appearance is beautiful in multi-layer narrow gap welding of thick plates. Ty.sj101 for gas pipes welding.Welding speed: 120mhagglomerated flux production line(total:three): wire yieldpoints(mpa) tensilestrengthb(mpa) elongation5(%) charpy v notch impact strength akv(j)-20c -40c -50cem12k 400 490-600 22 60 eh14 420 510-600 22 70 57 27eg 460 530-690 22 90 80 42ea2 500 600-700 20 60 55 34 cautions: damp flux should be re-dried at 300-350 centigrade for 2 hours.Rust, grease and moisture on the weldment should be removed before welding.

We are offering Welding Flux (sj301). Welding supply TY. SJ301Certification: ABS, CCSQuality system: ISO9001: 2008 Specification: AWS-A5.17 F6A0-EL8 F7A2-EM12KEN760 SA CS 1 89 AC H5 Equivalent to Lincoln 860 welding flux Applications: Butt and fillet welding ofMinature LPG tanks, Structural steels, Gas bottles, Pipeline steel, Especially Spiral pipes welding. Characteristics: 1. TY. SJ301 is an agglomerated calcium-silicate type welding flux 2. Metallurgical behavior: High silicon pick-up is obtained. When the manganese content in wire is less than 1.5%, also a manganese pick-up. 3. Grain size: 10 to 60 mesh Basicity: 1.0(BIIW) 4. Regularly shaped welds are deposited without reducion of area or interface notches. 5. Slag detachability is good. A short slag is produced, thus allowing circumferential welding on small-diameter workpieces without the risk of uncontrolled slag. 6. The production of large pipes(especially spiral pipe welding) is a typical application fo this flux 7. Relatively high manganese pick-up is obtained, thus allowing the flux to be used with wires with a low Mn content. Necessary process before welding: Damp flux should be re-dried at 300-350 C for 2 hours. Rust, grease and moisture on the weldment should be removed before welding. Our agglomerated flux production line: For Spiral pipes welding: ABS approval:

We are offering welding flux sj101. Weldingty. Sj101 agglomerated flux certification: abs company system: iso9001: 2008 max. Welding speed: 120mhour specification: aws a5.17 f6a0-el8 f7a2-em12k f7a4-eh14 applications1. Horizontal welding of oil storage tanks2. Fast welding of pipeline steel(x52, x60, x65, x70, x80 grade steels)3. Welding of thick-wallstructures of different kinds of high-tensile strength steel characteristics: 1. Ty-sj101 is an agglomerated fluoride-basic type flux. 2. Metallurgical behavior: slight silicon pick up. The behavior of manganese is neutral. 3. Basicity: 1.8(biiw). Grain size: 10 to 60 mesh 4. Welding performancety-sj101 assures excellent weldability, and the welding bead appearance is beautiful and the slag is easy to remove. 5. The diffusible hydrogen content in deposited metal is less than 5ml100g, so it has very good toughness at low temperature, therefore, crack resistance is extremely high. 6. It is suitable for submerged arc twin- wire, tandom and multi- wire welding as well as for welding with the two- run technique. cautions: damp flux should be re-dried at 300-35 centigrade for 2 hours. Rust, grease and moisture on the weldment should be removed before welding. ty. Sj101 for heavy steel structures welding

We are offering welding flux.Solder flux ty.sj301 specification: en760 sa cs 1 89 ac h5aws a5.17 f6a0-el8 f7a2-em12k usade 1 sj301 is fit for submerged arc welding of low-carbon steel and low-alloy steel 2 as well as the fast single-way and double-surface welding of thin plate 3 it is used for liquefied gas storage tanks, gas bottles and pipeline steel characteristics: 1. Ty.sj301 is an agglomerated calcium-silicate type welding flux 2. Grain size: 10 to 60 mesh 3. It has the properties of fine slag detachability and fine welding bead appearance. 4.the production of large pipes(especially spiral pipe welding) is a typical application fo this flux 5. Either alternate or direct current can be used application butt and fillet welding of minature lpg tanks, structural steels, gas bottles, pipeline steel, especially spiral pipes welding. wirestandard yield points(mpa) tensile strength b(mpa) elongation 5(%) impact valueakv (j)el8 f6a0-el8 350 420 22 40( 0c)em12k f7a2-em12k 410 500 30 60 (-20c) necessary process before welding: damp flux should be re-dried at 300-350 c for 2 hours.rust, grease and moisture on the weldment should be removed before welding.