We are a well-known as the leading Manufacturer and Supplier of the finest ABS FR V0. The ABS FR V0 provided by us is processed using the highest quality chemicals and thus is widely used in various Industries. We offer ABS FR V0 at affordable prices to the clients.

Grade :- SN06

Description	Unit	Value	ASTM
Specific Gravity	-	1.17 - 1.174	D 792
Melt Flow Rate @ 220oC / 10 kg	g/10 min	20 min	D 1238
Molding Shrinkage 3.2 mmsection	%	0.40 - 0.60	D 955
Mechanical
Impact Strength, Izod	-	-	-
notched 1/8 in (3.2 mm) section	J/m	80 min	D 256
Tensile Strength @ 50mm/min	MPa	44 min	D 638
Tensile Elongation@ yield 50mm/min	%	> 8.0	D 638
Flexural Strength 2mm/min	MPa	50 min	D 790
Flexural Modulus 2mm/min	MPa	1800 min	D 790
Thermal
Heat Deflection Temperature	-	-	-
@ 264 psi (1820 kPa)	oC	82 min	D 648
Vicat Softening- Method B	oC	96 Min	D 648
Flammability @ 3mm	-	V0	UL94
General Processing for Injection Molding
Injection Pressure	MPa	70 - 101	-
Melt Temperature	oC	206 - 236	-
Mold Temperature	oC	65- 86	-
Drying	hr @ oC	2 @ 80	-

Data herein is typical and not to be construed as specifications. Unless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties.The Above mentioned tchnical data is purely indicative and is given without any guarantee.

We are the chief Manufacturer and Supplier of the supreme ABS 10 GF, which is accurately synthesized by the proficient personnel. We also provide an option for the customized production of ABS 10 GF to cater to the needs of the clients, and that too within their budgets.

Grade :- SG29

Description	Unit	Value	ASTM
Specific Gravity	-	1.12 -1.13	D 792
Melt Flow Rate @ 230oC, / 2.16 kg	g/10 min	10 min	D 1238
Molding Shrinkage 3.2 mmsection	%	0.3 - 0.5	D 955
Mechanical
Impact Strength, Izod	-	-	-
notched 1/8 in (3.2 mm) section	J/m	60 - 75	D 256
Tensile Strength @ yield 50mm/min	MPa	60 Min	D 638
Tensile Modulus	MPa	4600 Min	D 638
Flexural Strength	MPa	90 Mim	D 790
Flexural Modulus	MPa	3700 Min	D 790
Thermal
Heat Deflection Temperature	-	-	-
@ 264 psi (1820 kPa)	oC	96 Min	D 648
@ 66 psi (455 kPa)	oC	100 Min	D 648
Flammability""	-	HB	UL94
General Processing for Injection Molding
Injection Pressure	MPa	68-102	-
Melt Temperature	oC	205-235	-
Mold Temperature	oC	60-80	-
Drying	hr @ oC	2@ 80	-

Data herein is typical and not to be construed as specifications.Unless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties.The Above mentioned tchnical data is purely indicative and is given without any guarantee

We are reckoned as one of the major ABS 15 GF Manufacturers and Suppliers from India. Our ABS 15 GF has gained us a lot of appreciation in the industry owing to its unique composition and quality. We offer ABS 15 GF at reasonable prices.

Grade :- SG39

Description	Unit	Value	ASTM Test
Specific Gravity	-	1.15 -1.16	D 792
Melt Flow Rate @ 230oC, / 2.16 kg	g/10 min	10 min	D 1238
Molding Shrinkage 3.2 mmsection	%	0.2 - 0.6	D 955
Mechanical
Impact Strength, Izod	-	-	-
notched 1/8 in (3.2 mm) section	J/m	50 Min	D 256
Tensile Strength @ yield 50mm/min	MPa	60 Min	D 638
Tensile Modulus	MPa	5000 Min	D 638
Flexural Strength	MPa	80 Mim	D 790
Flexural Modulus	MPa	3200 min	D 790
Thermal
Heat Deflection Temperature	-	-	-
@ 264 psi (1820 kPa)	oC	99 Min	D 648
@ 66 psi (455 kPa)	oC	101Min	D 648
Flammability""	-	HB	UL94
General Processing for Injection Molding
Injection Pressure	MPa	68-102	-
Melt Temperature	oC	205-235	-
Mold Temperature	oC	60-80	-
Drying	hr @ oC	2@ 80	-

Data herein is typical and not to be construed as specifications.Unless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties.The Above mentioned tchnical data is purely indicative and is given without any guarantee

We are known as the leading Manufacturer and Supplier of the superlative ABS 20 GF. Our ABS 20 GF is available in a wide variety and at the most competitive prices.

Grade :- SG49

Description	Unit	Value	ASTM Test
Specific Gravity	-	1.18 +- 0.1	D 792
Melt Flow Rate @ 220oC, / 10 kg	g/10 min	10 min	D 1238
Molding Shrinkage 3.2 mm section	%	0.1 -0.3	D 955
Mechanical
Impact Strength, Izod	-	-	-
Notched 1/8 in (6.2 mm) section	J/m	40 Min	D 256
Tensile Strength @ yield 50mm/min	MPa	62 Min	D 638
Tensile Modulus 50mm/min	MPa	5200 Min	D 638
Flexural Strength 2mm/min	MPa	82 Min	D 790
Flexural Modulus 2mm/min	MPa	3600 Min	D 790
Thermal
Heat Deflection Temperature	-	-	-
@ 264 psi (1820 kPa)	oC	101	D 648
@ 66 psi (455 kPa)	oC	103	D 648
Flammability""	-	HB	UL94
General Processing for Injection Molding
Injection Pressure	MPa	69 - 102	-
Melt Temperature	oC	205 - 240	-
Mold Temperature	oC	60 - 85	-
Drying	hr @ oC	2 @ 80	-

Data herein is typical and not to be construed as specifications.Unless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties.The Above mentioned tchnical data is purely indicative and is given without any guarantee

We introduce ourselves as one of the foremost ABS 25 GF Manufacturers and Suppliers, located in Bangalore. The demand for our ABS 25 GF has increased manifolds in so many years owing to its quality and cost effective features.

Grade :- SG59

Description	Unit	Value	ASTM
Specific Gravity	-	1.22 -1.23	D 792
Melt Flow Rate @ 230oC, / 2.16 kg	g/10 min	8 min	D 1238
Molding Shrinkage 3.2 mmsection	%	0.1 - 0.2	D 955
Mechanical
Impact Strength, Izod	-	-	-
notched 1/8 in (3.2 mm) section	J/m	50 Min	D 256
Tensile Strength @ yield 50mm/min	MPa	80 Min	D 638
Tensile Modulus	MPa	6500 Min	D 638
Flexural Strength	MPa	90 Mim	D 790
Flexural Modulus	MPa	5200 min	D 790
Thermal
Heat Deflection Temperature	-	-	-
@ 264 psi (1820 kPa)	oC	102 Min	D 648
@ 66 psi (455 kPa)	oC	105Min	D 648
Flammability""	-	HB	UL94
General Processing for Injection Molding
Injection Pressure	MPa	69-102	-
Melt Temperature	oC	205-235	-
Mold Temperature	oC	60-85	-
Drying	hr @ oC	2@ 80	-

Data herein is typical and not to be construed as specifications.Unless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties.The Above mentioned tchnical data is purely indicative and is given without any guarantee

We are reckoned as the prime Manufacturer and Supplier of the supreme ABS 30 GF. Our professionals very carefully carry out the task of synthesizing ABS 30 GF, with the helps of the finest chemicals. We offer ABS 30 GF at affordable prices to the clients.

Grade :- SG69

Description	Unit	Value	ASTM
Specific Gravity	-	1.21 -1.25	D 792
Melt Flow Rate @ 190oC, / 2.16 kg	g/10 min	8 min	D 1238
Molding Shrinkage 3.2 mmsection	%	0.1 - 0.3	D 955
Mechanical
Impact Strength, Izod	-	-
notched 1/8 in (3.2 mm) section	J/m	40 Min	D 256
Tensile Strength @ yield 50mm/min	MPa	72 Min	D 638
Tensile Modulus	MPa	6600 Min	D 638
Flexural Strength	MPa	87 Mim	D 790
Flexural Modulus	MPa	4800 min	D 790
Thermal
Heat Deflection Temperature	-	-	-
@ 264 psi (1820 kPa)	oC	102 Min	D 648
@ 66 psi (455 kPa)	oC	105Min	D 648
Flammability""	-	HB	UL94
General Processing for Injection Molding
Injection Pressure	MPa	68-102	-
Melt Temperature	oC	205-235	-
Mold Temperature	oC	60-85	-
Drying	hr @ oC	2 @ 80	-

Data herein is typical and not to be construed as specifications.Unless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties.The Above mentioned tchnical data is purely indicative and is given without any guarantee

We are the key PC 10% GF Manufacturer and Supplier, located in Karnataka. Our PC 10% GF is highly demanded by the clients owing to its finest quality and composition. We offer the PC 10% GF at the most competitive process to the clients.

Grade :- MG29

Description	Unit	Value	ASTM Test
Filler content	%	-	-
Specific Gravity	-	-	D 792
Melt Flow Rate @ 230 oC, / 2.16 kg	g/10 min	-	D 1238
Molding Shrinkage 3.2 mmsection	Molding Shrinkage 3.2 mmsection	-	D 955
Mechanical
Impact Strength, Izod	-	-	-
notched 1/8 in (3.2 mm) section	J/m	-	D 256
Tensile Strength	MPa	-	D 638
Tensile Elongation	%	-	D 638
Tensile Modulus	MPa	-	D 638
Flexural Strength	MPa	-	D 790
Flexural Modulus	MPa	-	D 790
Thermal
Heat Deflection Temperature	-	-	-
@ 264 psi (1820 kPa)	oC	-	D 648
@ 66 psi (455 kPa)	oC	-	D 648
Flammability""	-	V0	UL94
General Processing for Injection Molding
Injection Pressure	MPa	-	-
Melt Temperature	hr @ oC	-	-
Mold Temperature	oC	-	-
Drying	hr @ oC	-	-

This information provided hereon is based on tests believed to be reliable.However, this data is not guaranteed and no warranty, either expressed or implied is made concerning the use of this information or the use of the product described, whether or not known to the GLS Polymers Pvt Ltd.all data listed is for natural or black colored materials. Pigments can affect properties.

We are the well known Manufacturer and Supplier of the outstanding PC 20% GF. The PC 20% GF provided by us is vigilantly synthesized by the experts, with the help of the finest chemicals. We offer the PC 20% GF at affordable prices.

Grade :- MG49

Description	Unit	Value	ASTM Test
Filler content	%	-	-
Specific Gravity	-	-	D 792
Melt Flow Rate @ 230 oC, / 2.16 kg	g/10 min	-	D 1238
Molding Shrinkage 3.2 mmsection	Molding Shrinkage 3.2 mmsection	-	D 955
Mechanical
Impact Strength, Izod	-	-	-
notched 1/8 in (3.2 mm) section	J/m	-	D 256
Tensile Strength	MPa	-	D 638
Tensile Elongation	%	-	D 638
Tensile Modulus	MPa	-	D 638
Flexural Strength	MPa	-	D 790
Flexural Modulus	MPa	-	D 790
Thermal
Heat Deflection Temperature	-	-	-
@ 264 psi (1820 kPa)	oC	-	D 648
@ 66 psi (455 kPa)	oC	-	D 648
Flammability""	-	V0	UL94
General Processing for Injection Molding
Injection Pressure	MPa	-	-
Melt Temperature	hr @ oC	-	-
Mold Temperature	oC	-	-
Drying	hr @ oC	-	-

This information provided hereon is based on tests believed to be reliable.However, this data is not guaranteed and no warranty, either expressed or implied is made concerning the use of this information or the use of the product described, whether or not known to the GLS Polymers Pvt Ltd.all data listed is for natural or black colored materials. Pigments can affect properties.

We are known as one of the chief Manufacturers and Suppliers of the quality Nylon6 FR V0. Our Nylon6 FR V0 serves the varying industrial requirements of the widely spread clients. Our Nylon6 FR V0 is popular for its quality and unique composition and also for its cost effective feature.

Grade :- PN06

Description	Unit	Value	ASTM
Specific Gravity	-	1.15 - 1.16	D 792
Molding Shrinkage 3.2 mm section	%	1.2 - 1.8	D 955
Mechanical
Impact Strength, Izod	-	-	-
Notched 1/8 in (3.2 mm) section	J/m	35 min	D 256
Tensile Strength @ 50mm/min	MPa	62 min	D 638
Tensile Elongation@ yield 50mm/min	%	> 3.0	D 638
Flexural Strength 2mm/min	MPa	90 min	D 790
Flexural Modulus 2mm/min	MPa	2800 min	D 790
Thermal
Heat Deflection Temperature	-	-	-
@ 264 psi (1820 kPa)	oC	70 min	D 648
@ 66 psi (455 kPa)	oC	200 min	D 648
Flammability @ 3mm	-	V0	UL94
General Processing for Injection Molding
Injection Pressure	MPa	70 -105	-
Melt Temperature	oC	240 - 280	-
Mold Temperature	oC	55 - 95	-
Drying	hr @ oC	3 @ 85	-

Data herein is typical and not to be construed as specifications.Unless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties.The Above mentioned tchnical data is purely indicative and is given without any guarantee

We are the key Manufacturer and Supplier of the finest Nylon6 15 GF. We offer the customized production facility for our Nylon6 15 GF, to cater to the specific requirements of the clients. The Nylon6 15 GF can be availed at competitive prices.

Grade :- PG39

Description	Unit	Value	ASTM
Specific Gravity	-	1.20 - 1.24	D 792
Molding Shrinkage 3.2 mmsection	%	0.3-0.6	D 955
Mechanical
Impact Strength, Izod	-	-	-
notched 1/8 in (3.2 mm) section	J/m	40 min	D 256
Tensile Strength YIield@ 50mm/min	MPa	100 min	D 638
Tensile Elongation@ break 50mm/min	%	2-6	D 638
Flexural Strength 2mm/min	MPa	130 min	D 790
Flexural Modulus 2mm/min	MPa	4000 min	D 790
Thermal
Heat Deflection Temperature	-	-	-
@ 264 psi (1820 kPa)	oC	58 min	D 648
@ 66 psi (455 kPa)	oC	150 min	D 648
Vicat Softening- Method B	oC	210 Min	D 648
Flammability @ 3mm	-	HB	UL94
General Processing for Injection Molding
Injection Pressure	MPa	68 - 105	-
Melt Temperature	oC	245- 280	-
Mold Temperature	oC	55-95	-
Drying	hr @ oC	3 @ 85	-

Data herein is typical and not to be construed as specifications.Unless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties.The Above mentioned tchnical data is purely indicative and is given without any guarantee

We are the prime Nylon6 20 GF Manufacturer and Supplier in India. We offer a wide range of Nylon6 20 GF at the market leading to the clients. Our Nylon6 20 GF is widely used for various industrial applications.

We are one of the prime Manufacturer and Supplier of the superlative Nylon6 25 GF. The demand for our Nylon6 25 GF has gradually increased over the time period, owing to its quality and excellent composition. The Nylon6 25 GF can be availed at the most competitive prices from us.

Grade :- PG49

Description	Unit	Value	ASTM Test
Filler content	%	-	-
Specific Gravity	-	-	D 792
Melt Flow Rate @ 230 oC, / 2.16 kg	g/10 min	-	D 1238
Molding Shrinkage 3.2 mmsection	%	-	D 955
Mechanical
Impact Strength, Izod	-	-	-
notched 1/8 in (3.2 mm) section	J/m	-	D 256
Tensile Strength	MPa	-	D 638
Tensile Elongation	%	-	D 638
Tensile Modulus	MPa	-	D 638
Flexural Strength	MPa	-	D 790
Flexural Modulus	MPa	-	D 790
Thermal
Heat Deflection Temperature	-	-	-
@ 264 psi (1820 kPa)	oC	-	D 648
@ 66 psi (455 kPa)	oC	-	D 648
Flammability""	-	V0	UL94
General Processing for Injection Molding
Injection Pressure	MPa	-	-
Melt Temperature	oC	-	-
Mold Temperature	oC	-	-
Drying	hr @ oC	-	-

This information provided hereon is based on tests believed to be reliable.However, this data is not guaranteed and no warranty, either expressed or implied is made concerning the use of this information or the use of the product described, whether or not known to the GLS Polymers Pvt Ltd.all data listed is for natural or black colored materials. Pigments can affect properties.

We are reckoned as the chief Nylon6 30 GF Manufacturer and Supplier, based in India. A flawless range of Nylon6 30 GF is provided by the company at the most competitive prices. Our Nylon6 30 GF is used for various industrial applications.

Grade :- PG69

Description	Unit	Value	ASTM
Specific Gravity	-	1.33 - 1.37	D 792
Molding Shrinkage 3.2 mmsection	%	0.2-0.4	D 955
Mechanical
Impact Strength, Izod	-	-	-
notched 1/8 in (3.2 mm) section	J/m	70 min	D 256
Tensile Strength @ 50mm/min	MPa	140 min	D 638
Tensile Elongation@ yield 50mm/min	%	2.0 - 4.0	D 638
Flexural Strength 2mm/min	MPa	175 min	D 790
Flexural Modulus 2mm/min	MPa	7500 min	D 790
Thermal
Heat Deflection Temperature	-	-	-
@ 264 psi (1820 kPa)	oC	201 min	D 648
@ 66 psi (455 kPa)	oC	210 min	D 648
Vicat Softening- Method B	oC	215 Min	D 648
Flammability @ 3.2 mm	-	HB	UL94
General Processing for Injection Molding
Injection Pressure	MPa	68 - 105	-
Melt Temperature	oC	245- 280	-
Mold Temperature	oC	55-95	-
Drying	hr @ oC	3 @ 85	-

Data herein is typical and not to be construed as specifications.Unless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties.The Above mentioned tchnical data is purely indicative and is given without any guarantee

The company is considered as the key Nylon66 15 GF Manufacturer and Supplier in India. A wide assortment of Nylon66 15 GF is available at the market leading prices for the widely spread clients.

Grade :- LG39

Description	Unit	Value	ASTM Test
Filler content	%	-	-
Specific Gravity	-	-	D 792
Melt Flow Rate @ 230 oC, / 2.16 kg	g/10 min	-	D 1238
Molding Shrinkage 3.2 mmsection	%	-	D 955
Mechanical
Impact Strength, Izod	-	-	-
notched 1/8 in (3.2 mm) section	J/m	-	D 256
Tensile Strength	MPa	-	D 638
Tensile Elongation	%	-	D 638
Tensile Modulus	MPa	-	D 638
Flexural Strength	MPa	-	D 790
Flexural Modulus	MPa	-	D 790
Thermal
Heat Deflection Temperature	-	-	-
@ 264 psi (1820 kPa)	oC	-	D 648
@ 66 psi (455 kPa)	oC	-	D 648
Flammability""	-	V0	UL94
General Processing for Injection Molding
Injection Pressure	MPa	-	-
Melt Temperature	oC	-	-
Mold Temperature	oC	-	-
Drying	hr @ oC	-	-

This information provided hereon is based on tests believed to be reliable.However, this data is not guaranteed and no warranty, either expressed or implied is made concerning the use of this information or the use of the product described, whether or not known to the GLS Polymers Pvt Ltd.all data listed is for natural or black colored materials. Pigments can affect properties.

We introduce ourselves as the leading Manufacturer and Supplier of the outstanding Nylon66 20 GF. Our Nylon66 20 GF is highly acknowledged amongst the end users, due to their efficiency and composition. We offer Nylon66 20 GF at competitive prices to the clients.

Grade :- LG49

Description	Unit	Value	ASTM Test
Filler content	%	-	-
Specific Gravity	-	-	D 792
Melt Flow Rate @ 230 oC, / 2.16 kg	g/10 min	-	D 1238
Molding Shrinkage 3.2 mmsection	%	-	D 955
Mechanical
Impact Strength, Izod	-	-	-
notched 1/8 in (3.2 mm) section	J/m	-	D 256
Tensile Strength	MPa	-	D 638
Tensile Elongation	%	-	D 638
Tensile Modulus	MPa	-	D 638
Flexural Strength	MPa	-	D 790
Flexural Modulus	MPa	-	D 790
Thermal
Heat Deflection Temperature	-	-	-
@ 264 psi (1820 kPa)	oC	-	D 648
@ 66 psi (455 kPa)	oC	-	D 648
Flammability""	-	V0	UL94
General Processing for Injection Molding
Injection Pressure	MPa	-	-
Melt Temperature	oC	-	-
Mold Temperature	oC	-	-
Drying	hr @ oC	-	-

This information provided hereon is based on tests believed to be reliable.However, this data is not guaranteed and no warranty, either expressed or implied is made concerning the use of this information or the use of the product described, whether or not known to the GLS Polymers Pvt Ltd.all data listed is for natural or black colored materials. Pigments can affect properties.

We are counted amongst the major Manufacturers and Suppliers of the finest PP FR V0 in India. We offer a wide assortment of the PP FR V0, which is manufactured using the advanced technology, under the supervision of the experts. The PP FR V0 can be availed at reasonable prices from us.

Grade :- YN06

Description	Unit	Value	ASTM Test
Filler content	%	-	-
Specific Gravity	-	-	D 792
Melt Flow Rate @ 230oC, / 2.16 kg	g/10 min	-	D 1238
Molding Shrinkage 3.2 mmsection	%	-	D 955
Mechanical
Impact Strength, Izod	-	-	-
notched 1/8 in (3.2 mm) section	J/m	-	D 256
Tensile Strength	MPa	-	D 638
Tensile Elongation	%	-	D 638
Tensile Modulus	MPa	-	D 638
Flexural Strength	MPa		D 790
Flexural Modulus	MPa	-	D 790
Thermal
Heat Deflection Temperature	-	-	-
@ 264 psi (1820 kPa)	oC	-	D 648
@ 66 psi (455 kPa)	oC	-	D 648
Flammability""	-	V0	UL94
General Processing for Injection Molding
Injection Pressure	MPa	-	-
Melt Temperature	oC	-	-
Mold Temperature	oC	-	-
Drying	hr @ oC	-	-

This information provided hereon is based on tests believed to be reliable.However, this data is not guaranteed and no warranty, either expressed or implied is made concerning the use of this information or the use of the product described, whether or not known to the GLS Polymers Pvt Ltd.all data listed is for natural or black colored materials. Pigments can affect properties.

We are the chief PP 20 Talc FR V0 Manufacturer and Supplier, located in Bangalore. Our PP 20 Talc FR V0 is available in a wide range and at the market leading prices for the esteemed clients.

Grade :- YT46

Description	Unit	Value	ASTM Test
Filler content	%	-	-
Specific Gravity	-	-	D 792
Melt Flow Rate @ 230 oC, / 2.16 kg	g/10 min	-	D 1238
Molding Shrinkage 3.2 mmsection	%	-	D 955
Mechanical
Impact Strength, Izod	-	-	-
notched 1/8 in (3.2 mm) section	J/m	-	D 256
Tensile Strength	MPa	-	D 638
Tensile Elongation	%	-	D 638
Tensile Modulus	MPa	-	D 638
Flexural Strength	MPa	-	D 790
Flexural Modulus	MPa	-	D 790
Thermal
Heat Deflection Temperature	-	-	-
@ 264 psi (1820 kPa)	oC	-	D 648
@ 66 psi (455 kPa)	oC	-	D 648
Flammability""	-	V0	UL94
General Processing for Injection Molding
Injection Pressure	MPa	-	-
Melt Temperature	oC	-	-
Mold Temperature	oC	-	-
Drying	hr @ oC	-	-

This information provided hereon is based on tests believed to be reliable.However, this data is not guaranteed and no warranty, either expressed or implied is made concerning the use of this information or the use of the product described, whether or not known to the GLS Polymers Pvt Ltd.all data listed is for natural or black colored materials. Pigments can affect properties.

We are a well-known as the leading Manufacturer and Supplier of the finest ABS FR V0. The ABS FR V0 provided by us is processed using the highest quality chemicals and thus is widely used in various Industries. We offer ABS FR V0 at affordable prices to the clients.

Grade :- SN06

Description	Unit	Value	ASTM
Specific Gravity	-	1.17 - 1.174	D 792
Melt Flow Rate @ 220oC / 10 kg	g/10 min	20 min	D 1238
Molding Shrinkage 3.2 mmsection	%	0.40 - 0.60	D 955
Mechanical
Impact Strength, Izod	-	-	-
notched 1/8 in (3.2 mm) section	J/m	80 min	D 256
Tensile Strength @ 50mm/min	MPa	44 min	D 638
Tensile Elongation@ yield 50mm/min	%	> 8.0	D 638
Flexural Strength 2mm/min	MPa	50 min	D 790
Flexural Modulus 2mm/min	MPa	1800 min	D 790
Thermal
Heat Deflection Temperature	-	-	-
@ 264 psi (1820 kPa)	oC	82 min	D 648
Vicat Softening- Method B	oC	96 Min	D 648
Flammability @ 3mm	-	V0	UL94
General Processing for Injection Molding
Injection Pressure	MPa	70 - 101	-
Melt Temperature	oC	206 - 236	-
Mold Temperature	oC	65- 86	-
Drying	hr @ oC	2 @ 80	-

Data herein is typical and not to be construed as specifications. Unless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties.The Above mentioned tchnical data is purely indicative and is given without any guarantee.

We are the chief Manufacturer and Supplier of the supreme ABS 10 GF, which is accurately synthesized by the proficient personnel. We also provide an option for the customized production of ABS 10 GF to cater to the needs of the clients, and that too within their budgets.

Grade :- SG29

Description	Unit	Value	ASTM
Specific Gravity	-	1.12 -1.13	D 792
Melt Flow Rate @ 230oC, / 2.16 kg	g/10 min	10 min	D 1238
Molding Shrinkage 3.2 mmsection	%	0.3 - 0.5	D 955
Mechanical
Impact Strength, Izod	-	-	-
notched 1/8 in (3.2 mm) section	J/m	60 - 75	D 256
Tensile Strength @ yield 50mm/min	MPa	60 Min	D 638
Tensile Modulus	MPa	4600 Min	D 638
Flexural Strength	MPa	90 Mim	D 790
Flexural Modulus	MPa	3700 Min	D 790
Thermal
Heat Deflection Temperature	-	-	-
@ 264 psi (1820 kPa)	oC	96 Min	D 648
@ 66 psi (455 kPa)	oC	100 Min	D 648
Flammability""	-	HB	UL94
General Processing for Injection Molding
Injection Pressure	MPa	68-102	-
Melt Temperature	oC	205-235	-
Mold Temperature	oC	60-80	-
Drying	hr @ oC	2@ 80	-

Data herein is typical and not to be construed as specifications.Unless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties.The Above mentioned tchnical data is purely indicative and is given without any guarantee

We are reckoned as one of the major ABS 15 GF Manufacturers and Suppliers from India. Our ABS 15 GF has gained us a lot of appreciation in the industry owing to its unique composition and quality. We offer ABS 15 GF at reasonable prices.

Grade :- SG39

Description	Unit	Value	ASTM Test
Specific Gravity	-	1.15 -1.16	D 792
Melt Flow Rate @ 230oC, / 2.16 kg	g/10 min	10 min	D 1238
Molding Shrinkage 3.2 mmsection	%	0.2 - 0.6	D 955
Mechanical
Impact Strength, Izod	-	-	-
notched 1/8 in (3.2 mm) section	J/m	50 Min	D 256
Tensile Strength @ yield 50mm/min	MPa	60 Min	D 638
Tensile Modulus	MPa	5000 Min	D 638
Flexural Strength	MPa	80 Mim	D 790
Flexural Modulus	MPa	3200 min	D 790
Thermal
Heat Deflection Temperature	-	-	-
@ 264 psi (1820 kPa)	oC	99 Min	D 648
@ 66 psi (455 kPa)	oC	101Min	D 648
Flammability""	-	HB	UL94
General Processing for Injection Molding
Injection Pressure	MPa	68-102	-
Melt Temperature	oC	205-235	-
Mold Temperature	oC	60-80	-
Drying	hr @ oC	2@ 80	-

Data herein is typical and not to be construed as specifications.Unless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties.The Above mentioned tchnical data is purely indicative and is given without any guarantee

We are known as the leading Manufacturer and Supplier of the superlative ABS 20 GF. Our ABS 20 GF is available in a wide variety and at the most competitive prices.

Grade :- SG49

Description	Unit	Value	ASTM Test
Specific Gravity	-	1.18 +- 0.1	D 792
Melt Flow Rate @ 220oC, / 10 kg	g/10 min	10 min	D 1238
Molding Shrinkage 3.2 mm section	%	0.1 -0.3	D 955
Mechanical
Impact Strength, Izod	-	-	-
Notched 1/8 in (6.2 mm) section	J/m	40 Min	D 256
Tensile Strength @ yield 50mm/min	MPa	62 Min	D 638
Tensile Modulus 50mm/min	MPa	5200 Min	D 638
Flexural Strength 2mm/min	MPa	82 Min	D 790
Flexural Modulus 2mm/min	MPa	3600 Min	D 790
Thermal
Heat Deflection Temperature	-	-	-
@ 264 psi (1820 kPa)	oC	101	D 648
@ 66 psi (455 kPa)	oC	103	D 648
Flammability""	-	HB	UL94
General Processing for Injection Molding
Injection Pressure	MPa	69 - 102	-
Melt Temperature	oC	205 - 240	-
Mold Temperature	oC	60 - 85	-
Drying	hr @ oC	2 @ 80	-

Data herein is typical and not to be construed as specifications.Unless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties.The Above mentioned tchnical data is purely indicative and is given without any guarantee

We introduce ourselves as one of the foremost ABS 25 GF Manufacturers and Suppliers, located in Bangalore. The demand for our ABS 25 GF has increased manifolds in so many years owing to its quality and cost effective features.

Grade :- SG59

Description	Unit	Value	ASTM
Specific Gravity	-	1.22 -1.23	D 792
Melt Flow Rate @ 230oC, / 2.16 kg	g/10 min	8 min	D 1238
Molding Shrinkage 3.2 mmsection	%	0.1 - 0.2	D 955
Mechanical
Impact Strength, Izod	-	-	-
notched 1/8 in (3.2 mm) section	J/m	50 Min	D 256
Tensile Strength @ yield 50mm/min	MPa	80 Min	D 638
Tensile Modulus	MPa	6500 Min	D 638
Flexural Strength	MPa	90 Mim	D 790
Flexural Modulus	MPa	5200 min	D 790
Thermal
Heat Deflection Temperature	-	-	-
@ 264 psi (1820 kPa)	oC	102 Min	D 648
@ 66 psi (455 kPa)	oC	105Min	D 648
Flammability""	-	HB	UL94
General Processing for Injection Molding
Injection Pressure	MPa	69-102	-
Melt Temperature	oC	205-235	-
Mold Temperature	oC	60-85	-
Drying	hr @ oC	2@ 80	-

Data herein is typical and not to be construed as specifications.Unless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties.The Above mentioned tchnical data is purely indicative and is given without any guarantee

We are reckoned as the prime Manufacturer and Supplier of the supreme ABS 30 GF. Our professionals very carefully carry out the task of synthesizing ABS 30 GF, with the helps of the finest chemicals. We offer ABS 30 GF at affordable prices to the clients.

Grade :- SG69

Description	Unit	Value	ASTM
Specific Gravity	-	1.21 -1.25	D 792
Melt Flow Rate @ 190oC, / 2.16 kg	g/10 min	8 min	D 1238
Molding Shrinkage 3.2 mmsection	%	0.1 - 0.3	D 955
Mechanical
Impact Strength, Izod	-	-
notched 1/8 in (3.2 mm) section	J/m	40 Min	D 256
Tensile Strength @ yield 50mm/min	MPa	72 Min	D 638
Tensile Modulus	MPa	6600 Min	D 638
Flexural Strength	MPa	87 Mim	D 790
Flexural Modulus	MPa	4800 min	D 790
Thermal
Heat Deflection Temperature	-	-	-
@ 264 psi (1820 kPa)	oC	102 Min	D 648
@ 66 psi (455 kPa)	oC	105Min	D 648
Flammability""	-	HB	UL94
General Processing for Injection Molding
Injection Pressure	MPa	68-102	-
Melt Temperature	oC	205-235	-
Mold Temperature	oC	60-85	-
Drying	hr @ oC	2 @ 80	-

Data herein is typical and not to be construed as specifications.Unless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties.The Above mentioned tchnical data is purely indicative and is given without any guarantee

We are the key PC 10% GF Manufacturer and Supplier, located in Karnataka. Our PC 10% GF is highly demanded by the clients owing to its finest quality and composition. We offer the PC 10% GF at the most competitive process to the clients.

Grade :- MG29

Description	Unit	Value	ASTM Test
Filler content	%	-	-
Specific Gravity	-	-	D 792
Melt Flow Rate @ 230 oC, / 2.16 kg	g/10 min	-	D 1238
Molding Shrinkage 3.2 mmsection	Molding Shrinkage 3.2 mmsection	-	D 955
Mechanical
Impact Strength, Izod	-	-	-
notched 1/8 in (3.2 mm) section	J/m	-	D 256
Tensile Strength	MPa	-	D 638
Tensile Elongation	%	-	D 638
Tensile Modulus	MPa	-	D 638
Flexural Strength	MPa	-	D 790
Flexural Modulus	MPa	-	D 790
Thermal
Heat Deflection Temperature	-	-	-
@ 264 psi (1820 kPa)	oC	-	D 648
@ 66 psi (455 kPa)	oC	-	D 648
Flammability""	-	V0	UL94
General Processing for Injection Molding
Injection Pressure	MPa	-	-
Melt Temperature	hr @ oC	-	-
Mold Temperature	oC	-	-
Drying	hr @ oC	-	-

This information provided hereon is based on tests believed to be reliable.However, this data is not guaranteed and no warranty, either expressed or implied is made concerning the use of this information or the use of the product described, whether or not known to the GLS Polymers Pvt Ltd.all data listed is for natural or black colored materials. Pigments can affect properties.

We are the well known Manufacturer and Supplier of the outstanding PC 20% GF. The PC 20% GF provided by us is vigilantly synthesized by the experts, with the help of the finest chemicals. We offer the PC 20% GF at affordable prices.

Grade :- MG49

Description	Unit	Value	ASTM Test
Filler content	%	-	-
Specific Gravity	-	-	D 792
Melt Flow Rate @ 230 oC, / 2.16 kg	g/10 min	-	D 1238
Molding Shrinkage 3.2 mmsection	Molding Shrinkage 3.2 mmsection	-	D 955
Mechanical
Impact Strength, Izod	-	-	-
notched 1/8 in (3.2 mm) section	J/m	-	D 256
Tensile Strength	MPa	-	D 638
Tensile Elongation	%	-	D 638
Tensile Modulus	MPa	-	D 638
Flexural Strength	MPa	-	D 790
Flexural Modulus	MPa	-	D 790
Thermal
Heat Deflection Temperature	-	-	-
@ 264 psi (1820 kPa)	oC	-	D 648
@ 66 psi (455 kPa)	oC	-	D 648
Flammability""	-	V0	UL94
General Processing for Injection Molding
Injection Pressure	MPa	-	-
Melt Temperature	hr @ oC	-	-
Mold Temperature	oC	-	-
Drying	hr @ oC	-	-

This information provided hereon is based on tests believed to be reliable.However, this data is not guaranteed and no warranty, either expressed or implied is made concerning the use of this information or the use of the product described, whether or not known to the GLS Polymers Pvt Ltd.all data listed is for natural or black colored materials. Pigments can affect properties.

We are known as one of the chief Manufacturers and Suppliers of the quality Nylon6 FR V0. Our Nylon6 FR V0 serves the varying industrial requirements of the widely spread clients. Our Nylon6 FR V0 is popular for its quality and unique composition and also for its cost effective feature.

Grade :- PN06

Description	Unit	Value	ASTM
Specific Gravity	-	1.15 - 1.16	D 792
Molding Shrinkage 3.2 mm section	%	1.2 - 1.8	D 955
Mechanical
Impact Strength, Izod	-	-	-
Notched 1/8 in (3.2 mm) section	J/m	35 min	D 256
Tensile Strength @ 50mm/min	MPa	62 min	D 638
Tensile Elongation@ yield 50mm/min	%	> 3.0	D 638
Flexural Strength 2mm/min	MPa	90 min	D 790
Flexural Modulus 2mm/min	MPa	2800 min	D 790
Thermal
Heat Deflection Temperature	-	-	-
@ 264 psi (1820 kPa)	oC	70 min	D 648
@ 66 psi (455 kPa)	oC	200 min	D 648
Flammability @ 3mm	-	V0	UL94
General Processing for Injection Molding
Injection Pressure	MPa	70 -105	-
Melt Temperature	oC	240 - 280	-
Mold Temperature	oC	55 - 95	-
Drying	hr @ oC	3 @ 85	-

Data herein is typical and not to be construed as specifications.Unless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties.The Above mentioned tchnical data is purely indicative and is given without any guarantee

We are the key Manufacturer and Supplier of the finest Nylon6 15 GF. We offer the customized production facility for our Nylon6 15 GF, to cater to the specific requirements of the clients. The Nylon6 15 GF can be availed at competitive prices.

Grade :- PG39

Description	Unit	Value	ASTM
Specific Gravity	-	1.20 - 1.24	D 792
Molding Shrinkage 3.2 mmsection	%	0.3-0.6	D 955
Mechanical
Impact Strength, Izod	-	-	-
notched 1/8 in (3.2 mm) section	J/m	40 min	D 256
Tensile Strength YIield@ 50mm/min	MPa	100 min	D 638
Tensile Elongation@ break 50mm/min	%	2-6	D 638
Flexural Strength 2mm/min	MPa	130 min	D 790
Flexural Modulus 2mm/min	MPa	4000 min	D 790
Thermal
Heat Deflection Temperature	-	-	-
@ 264 psi (1820 kPa)	oC	58 min	D 648
@ 66 psi (455 kPa)	oC	150 min	D 648
Vicat Softening- Method B	oC	210 Min	D 648
Flammability @ 3mm	-	HB	UL94
General Processing for Injection Molding
Injection Pressure	MPa	68 - 105	-
Melt Temperature	oC	245- 280	-
Mold Temperature	oC	55-95	-
Drying	hr @ oC	3 @ 85	-

Data herein is typical and not to be construed as specifications.Unless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties.The Above mentioned tchnical data is purely indicative and is given without any guarantee

We are the prime Nylon6 20 GF Manufacturer and Supplier in India. We offer a wide range of Nylon6 20 GF at the market leading to the clients. Our Nylon6 20 GF is widely used for various industrial applications.

We are one of the prime Manufacturer and Supplier of the superlative Nylon6 25 GF. The demand for our Nylon6 25 GF has gradually increased over the time period, owing to its quality and excellent composition. The Nylon6 25 GF can be availed at the most competitive prices from us.

Grade :- PG49

Description	Unit	Value	ASTM Test
Filler content	%	-	-
Specific Gravity	-	-	D 792
Melt Flow Rate @ 230 oC, / 2.16 kg	g/10 min	-	D 1238
Molding Shrinkage 3.2 mmsection	%	-	D 955
Mechanical
Impact Strength, Izod	-	-	-
notched 1/8 in (3.2 mm) section	J/m	-	D 256
Tensile Strength	MPa	-	D 638
Tensile Elongation	%	-	D 638
Tensile Modulus	MPa	-	D 638
Flexural Strength	MPa	-	D 790
Flexural Modulus	MPa	-	D 790
Thermal
Heat Deflection Temperature	-	-	-
@ 264 psi (1820 kPa)	oC	-	D 648
@ 66 psi (455 kPa)	oC	-	D 648
Flammability""	-	V0	UL94
General Processing for Injection Molding
Injection Pressure	MPa	-	-
Melt Temperature	oC	-	-
Mold Temperature	oC	-	-
Drying	hr @ oC	-	-

This information provided hereon is based on tests believed to be reliable.However, this data is not guaranteed and no warranty, either expressed or implied is made concerning the use of this information or the use of the product described, whether or not known to the GLS Polymers Pvt Ltd.all data listed is for natural or black colored materials. Pigments can affect properties.

We are reckoned as the chief Nylon6 30 GF Manufacturer and Supplier, based in India. A flawless range of Nylon6 30 GF is provided by the company at the most competitive prices. Our Nylon6 30 GF is used for various industrial applications.

Grade :- PG69

Description	Unit	Value	ASTM
Specific Gravity	-	1.33 - 1.37	D 792
Molding Shrinkage 3.2 mmsection	%	0.2-0.4	D 955
Mechanical
Impact Strength, Izod	-	-	-
notched 1/8 in (3.2 mm) section	J/m	70 min	D 256
Tensile Strength @ 50mm/min	MPa	140 min	D 638
Tensile Elongation@ yield 50mm/min	%	2.0 - 4.0	D 638
Flexural Strength 2mm/min	MPa	175 min	D 790
Flexural Modulus 2mm/min	MPa	7500 min	D 790
Thermal
Heat Deflection Temperature	-	-	-
@ 264 psi (1820 kPa)	oC	201 min	D 648
@ 66 psi (455 kPa)	oC	210 min	D 648
Vicat Softening- Method B	oC	215 Min	D 648
Flammability @ 3.2 mm	-	HB	UL94
General Processing for Injection Molding
Injection Pressure	MPa	68 - 105	-
Melt Temperature	oC	245- 280	-
Mold Temperature	oC	55-95	-
Drying	hr @ oC	3 @ 85	-

Data herein is typical and not to be construed as specifications.Unless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties.The Above mentioned tchnical data is purely indicative and is given without any guarantee

The company is considered as the key Nylon66 15 GF Manufacturer and Supplier in India. A wide assortment of Nylon66 15 GF is available at the market leading prices for the widely spread clients.

Grade :- LG39

Description	Unit	Value	ASTM Test
Filler content	%	-	-
Specific Gravity	-	-	D 792
Melt Flow Rate @ 230 oC, / 2.16 kg	g/10 min	-	D 1238
Molding Shrinkage 3.2 mmsection	%	-	D 955
Mechanical
Impact Strength, Izod	-	-	-
notched 1/8 in (3.2 mm) section	J/m	-	D 256
Tensile Strength	MPa	-	D 638
Tensile Elongation	%	-	D 638
Tensile Modulus	MPa	-	D 638
Flexural Strength	MPa	-	D 790
Flexural Modulus	MPa	-	D 790
Thermal
Heat Deflection Temperature	-	-	-
@ 264 psi (1820 kPa)	oC	-	D 648
@ 66 psi (455 kPa)	oC	-	D 648
Flammability""	-	V0	UL94
General Processing for Injection Molding
Injection Pressure	MPa	-	-
Melt Temperature	oC	-	-
Mold Temperature	oC	-	-
Drying	hr @ oC	-	-

This information provided hereon is based on tests believed to be reliable.However, this data is not guaranteed and no warranty, either expressed or implied is made concerning the use of this information or the use of the product described, whether or not known to the GLS Polymers Pvt Ltd.all data listed is for natural or black colored materials. Pigments can affect properties.

We introduce ourselves as the leading Manufacturer and Supplier of the outstanding Nylon66 20 GF. Our Nylon66 20 GF is highly acknowledged amongst the end users, due to their efficiency and composition. We offer Nylon66 20 GF at competitive prices to the clients.

Grade :- LG49

Description	Unit	Value	ASTM Test
Filler content	%	-	-
Specific Gravity	-	-	D 792
Melt Flow Rate @ 230 oC, / 2.16 kg	g/10 min	-	D 1238
Molding Shrinkage 3.2 mmsection	%	-	D 955
Mechanical
Impact Strength, Izod	-	-	-
notched 1/8 in (3.2 mm) section	J/m	-	D 256
Tensile Strength	MPa	-	D 638
Tensile Elongation	%	-	D 638
Tensile Modulus	MPa	-	D 638
Flexural Strength	MPa	-	D 790
Flexural Modulus	MPa	-	D 790
Thermal
Heat Deflection Temperature	-	-	-
@ 264 psi (1820 kPa)	oC	-	D 648
@ 66 psi (455 kPa)	oC	-	D 648
Flammability""	-	V0	UL94
General Processing for Injection Molding
Injection Pressure	MPa	-	-
Melt Temperature	oC	-	-
Mold Temperature	oC	-	-
Drying	hr @ oC	-	-

This information provided hereon is based on tests believed to be reliable.However, this data is not guaranteed and no warranty, either expressed or implied is made concerning the use of this information or the use of the product described, whether or not known to the GLS Polymers Pvt Ltd.all data listed is for natural or black colored materials. Pigments can affect properties.

We are counted amongst the major Manufacturers and Suppliers of the finest PP FR V0 in India. We offer a wide assortment of the PP FR V0, which is manufactured using the advanced technology, under the supervision of the experts. The PP FR V0 can be availed at reasonable prices from us.

Grade :- YN06

Description	Unit	Value	ASTM Test
Filler content	%	-	-
Specific Gravity	-	-	D 792
Melt Flow Rate @ 230oC, / 2.16 kg	g/10 min	-	D 1238
Molding Shrinkage 3.2 mmsection	%	-	D 955
Mechanical
Impact Strength, Izod	-	-	-
notched 1/8 in (3.2 mm) section	J/m	-	D 256
Tensile Strength	MPa	-	D 638
Tensile Elongation	%	-	D 638
Tensile Modulus	MPa	-	D 638
Flexural Strength	MPa		D 790
Flexural Modulus	MPa	-	D 790
Thermal
Heat Deflection Temperature	-	-	-
@ 264 psi (1820 kPa)	oC	-	D 648
@ 66 psi (455 kPa)	oC	-	D 648
Flammability""	-	V0	UL94
General Processing for Injection Molding
Injection Pressure	MPa	-	-
Melt Temperature	oC	-	-
Mold Temperature	oC	-	-
Drying	hr @ oC	-	-

This information provided hereon is based on tests believed to be reliable.However, this data is not guaranteed and no warranty, either expressed or implied is made concerning the use of this information or the use of the product described, whether or not known to the GLS Polymers Pvt Ltd.all data listed is for natural or black colored materials. Pigments can affect properties.

We are the chief PP 20 Talc FR V0 Manufacturer and Supplier, located in Bangalore. Our PP 20 Talc FR V0 is available in a wide range and at the market leading prices for the esteemed clients.

Grade :- YT46

Description	Unit	Value	ASTM Test
Filler content	%	-	-
Specific Gravity	-	-	D 792
Melt Flow Rate @ 230 oC, / 2.16 kg	g/10 min	-	D 1238
Molding Shrinkage 3.2 mmsection	%	-	D 955
Mechanical
Impact Strength, Izod	-	-	-
notched 1/8 in (3.2 mm) section	J/m	-	D 256
Tensile Strength	MPa	-	D 638
Tensile Elongation	%	-	D 638
Tensile Modulus	MPa	-	D 638
Flexural Strength	MPa	-	D 790
Flexural Modulus	MPa	-	D 790
Thermal
Heat Deflection Temperature	-	-	-
@ 264 psi (1820 kPa)	oC	-	D 648
@ 66 psi (455 kPa)	oC	-	D 648
Flammability""	-	V0	UL94
General Processing for Injection Molding
Injection Pressure	MPa	-	-
Melt Temperature	oC	-	-
Mold Temperature	oC	-	-
Drying	hr @ oC	-	-

This information provided hereon is based on tests believed to be reliable.However, this data is not guaranteed and no warranty, either expressed or implied is made concerning the use of this information or the use of the product described, whether or not known to the GLS Polymers Pvt Ltd.all data listed is for natural or black colored materials. Pigments can affect properties.