Wood Plastic Composite (WPC) as the name suggests is a unique product which has features of both. From generations, we have faced one never ending problem, the damage to our precious furniture caused by termite, borer or seepage. But today, we have a product which can solve all our problems. WPC is made from Plastic and wood. The percentage of plastic in WPC is more than 80%, which makes it 100% Water Proof Termite Proof
There is an increasing demand of WPC Panel in our society because of its numerous advantages. we ensured a very good product in every aspect like colour, surface, hardness, strength, nail holding capacity. WPC can be used just like a plywood. Even all the tools and screws are same as plywood tools screws. The biggest challenge for every new product is to make carpenters learn about its usage but in the case of WPC, not even a bit of new learning is required for them.
Technical Specification
| Test Prescribed in IS:710 – 2010 |
Minimum Value for Conformity | Observed Value |
|---|---|---|
| Glue Shear Strength (after 72 hours boiling) | Min. Ind: 800 Avg: 1000 N |
N1150N 1240N |
| Moisture Content Test | Not less than 5% | 9% |
| Adhesive of Piles | Minimum Pass Standard | Excellent |
| Glue Shear Strength (Dry State) |
Min. Ind. 1100 N Avg. 1350 N |
1250 N 1450 N |
| Static Bending Strength (Dry) Modulus of Rupture -Along the grain -Across the grain Modulus of Elasticity -Along the grain _Across the grain |
Avg. 50 N/Sq.mm Avg. 30 N/Sq.mmAvg. 7500 N/Sq.mm Avg. 4000 N/Sq.mm |
63N/Sq.mm 38N/Sq.mm 9200N/Sq.mm 8295N/Sq.mm 4150N/Sq.mm |
| Static Bending Strength (Wet) Modulus of Rupture -Along the grain -Across the grain Modulus of Elasticity -Along the grain _Across the grain |
Avg. 25 N/Sq.mm Avg. 15 N/Sq.mmAvg. 3750 N/Sq.mm Avg. 2000 N/Sq.mm |
34N/Sq.mm 21N/Sq.mm 5440N/Sq.mm 2100N/Sq.mm |
| Tensile Strength -Along the grain -Across the garin Sum of tensile strength |
Avg. 42.00 N/Sq.mm Avg. 25.00 N/Sq.mm Avg. 84.50 N/Sq.mm |
53.00 N/Sq.mm 38N/Sq.mm 92.50N/Sq.mm |
| Retention of Preservative Chemicals Kg/Cbm (ACC Type) | Min 12kg/cbm | Min 12.9kg/cbm |
| Test Prescribed in IS:2202-(Part-1, 1999) | Minimum Value for Conformity | Observed Value |
|---|---|---|
| General Fitness Test as per IS:4020 (Part 3), 1998 | Squareness measured | Confirmed |
| Local Planeness Test as per IS:4020 (Part 4), 1998 | Planeness measured to ah accuracy of 0.1 m | Confirmed |
| Dimension and Squareness Test as per IS: 4020 (Part 2), 1998 | Height and Width measured within an accuracy of 1.0 mm | Confirmed |
| Impact indentation Test as per IS: 4020 (Part 5), 1998 | Indentation Measured to an accuracy of 0.1 mm | Confirmed |
| Edge Loading Test as per IS: 4020 (Part 7). 1998 | The deflection measured to an accuracy of 0.1 mm | Confirmed |
| Flexure Test as per IS: 4020 (Part 6), 1998 | The deflection measured to an accuracy of 0.1 mm | Confirmed |
| Slamming Test as per IS: 4020 (Part 10), 1998 | 50 times on the nail at the rate of 4-5 dropl min | Confirmed |
| Buckling Test as per IS: 4020 (Part 9). 1998 | Deformation measured to an accuracy of 1mm, 5 min. after application of the load and 15 min. after unloading | Confirmed |
| Shock Resistance Test as per IS: 4020 (Part 8), 1998 | 4 to 5 shocks minimum | Confirmed |
| Misuse Test as per IS: 4020 (Part 11), 1998 | Should pass after applying 2OON force to the handle at right angles | Confirmed |
| End Immersion Test as per IS:4020 (Part 13), 1998 | No-delamination | No-delamination found |
| Varying Humidity Test as per IS: 4020 (Part 12), 1998 | ‘Deviation measures to an accuracy of 1 .0 mm | Confirmed |
| Knief Test as per IS: 4020 (Part 14) 1998 | Minimum Pass Standard | Excellent Standard |
| Screw Withdraw as per IS: 4020 (Part 16), 1998 | Applied load should be 2.0 mm per min for complete withdrawal of the screw | Confirmed |
| Glue Adhesive Test as per IS: 4020 (Part 15), 1998 | There shall be no-delamination | No-delamination found |