We offer the best product range of HDPE pe100 Resin and HDPE Virgin Polyethylene PE Resin HDPE LDPE MDPE LLDPE Plastic Raw Material.
HDPE pe100 resin
HDPE high density polyethylene PE100 pipe grade HDPE plastic raw material HDPE granules
Type: Virgin Grade: Film Grade, Injection Grade, Blow molding Grade, Extrusion Grade, Pipe Grade.ect.
Color: Natural, Transparent, white .
Specification
Item
Test method
Test Date
Date Unit
Density
ASTM D-1505
0.955
g/cm
Melt Flow rate
ASTM D-1238
0.35
g/10min
Elongation at Break
ASTM D-638
600
Kg/cm
Tensile strength at 23 degree
ASTM D-638
27
Kg/cm
Additional Information:
Payment Terms : T/T, Western Union,
Packaging Details : buyers request
HDPE Virgin Polyethylene PE resin HDPE LDPE MDPE LLDPE plastic raw material
Specification
Grades
LD165
LDPE-2100TN00
LDPE-18G
LDPE-2426F
LDPE-2426H
Density, g/cm
0.9214
0.9192
0.918
0.923
0.923
MFR, g/10min
0.30
0.308
7
0.8
1.9
Stretching broken column nominal strain, %
548
529
-
MD200
TD600
600
Tensile strength at broken, Mpa
15.8
14.5
-
MD26
TD20
15
Haze, %
10
-
-
-
8
Fisheye(0.3mm-0.2mm), qty/1200cm
25
-
-
-
-
Swell ratio, /
-
-
1.55
-
-
Turbidity, %
-
-
-
40
-
Film Thickness, m
-
-
-
50
-
Modulus of Elasticity, Mpa
-
-
-
260
-
Dart Impact Strength, g
-
-
-
130
-
Vicat Softening Point,
-
-
-
94
-
DSC Melting Point,
-
-
-
11
-
Application
Tubular film
Tubular film
Film
Film
Film
Grades
LDPE-2420D
LDPE-1C7A
LD605
LD100BW
LDPE1l50A
Density, g/cm
0.9225
0.918
0.922
0.923
0.923
MFR, g/10min
0.25
7
6
2.1
50
Stretching broken column nominal strain, %
-
-
100
-
-
Tensile strength at broken, Mpa
10
-
8
11
6
Haze, %
15
-
-
-
-
Film Thickness, m
(60)50
-
-
-
-
Modulus of Elasticity, Mpa
240
-
-
-
-
Dart Impact Strength, g
-
-
-
-
-
Vicat Softening Point,
94
-
-
-
-
DSC Melting Point,
109
-
-
-
-
Application
Film, blow-molded hollow products
cardboard, packaging
civil detonators, pipes, plates and injection-molding products
Wire&Cable Grade