Degassers We are offering our clients with an appropriately prepared range of degassers that is used for degassing of Aluminum molten metal. This degassers gives the utmost degassing effect. It is used for all types of Aluminum and its different types of alloys. The application rate for this type of degasser is also about 0.2 %. Instructions After attaining the required metal temperature, shut off the furnace to have better degassing effect at falling temperature. Degasser tablet is to be slightly heated before use after removing the wrapper precaution is to be taken to avoid exposure of tablet to the atmosphere as it may pick up the moisture. Push the dross a little aside and plunge the recommended quantity of Daga Degasser using a preheated perforated bell plunger to the bottom of the melt. As soon as the bubbling stops remove the plunger after rabbling & skim off the dross. Advantages The use of Degasser is quite simple it does not require any special tool as equipment. It removes hydrogen gas, oxides and other impurities from the melt which results in superior finishing of the metal and avoids pinholes in the castings. Packing Daga Degasser are available in the shape of 50 Gms. & 250 Gms compact tablet form. The tablets are packed in 20 kgs & 40 kgs Box that is solid enough to withstand shakes and jolts of transportation.   More About Information of Degasser Tablets : Aluminium & its alloys are susceptible in absorbing gas even when the bestcontrolled melting processes are performed. There are many factors which cause absorption of Hydrogen gas like water vapour from atmosphere, damp scrap, damp tools, prolonged holding of metals etc. During the process of casting these unwanted gases release suddenly in the form of bubbles, which are trapped in the metal, and finally the development of pinhole porosity in the cast product occur. It is therefore necessary to remove the unwanted gas from the melt prior to pouring. DAGA DEGASSERS SP-II (Red) : Are formulated to remove hydrogen gas, oxides and other impurities from the melt which results in superior finishing of the metal and avoids pinholes in the castings It is used for all types of Aluminum and its different types of alloys. The application rate for this type of degasser is about 0.2 %. DAGA DGR SP-I (BLUE) : It is a very strong type of tablet, which is used for Degassing Aluminium and its alloys as well as Grain Refining also. Its application rate is about 0.2 %. Instructions : After attaining the required metal temperature, shut off the furnace to have better effect at falling temperature. DEGASSER or DGR tablet is to be slightly heated before use after removing the wrapper. The precaution is to be taken to avoid exposure of tablet to the atmosphere as it may pick up the moisture.Push the dross a little aside and plunge DEGASSER or DGR using a preheated perforated plunger to the bottom of the melt. As soon as the bubbling stops remove the plunger after rabbling, skim off the dross. Packing : DAGA DEGASSERS AND DAGA DGR’s are available in the shape of 50 Gms. & 250 Gms, packed in 25 kgs, 30 kgs & 40 kgs Boxes.

We are providing to our client Metafill Sp-I (EBT Filling Compound)..These are offering on market leading prices.Also offer this products as per client specification.   More About Eccentric Bottom Tapping (EBT) device is fitted with refractory on to the electric arc furnace. EBT filling mass is a selected refractory mass, which seals the refractory hole of EBT device during refining of steel in the arc furnace. Advantages " METAFILL SP – I " , the EBT filling mass has the following advantages: It doesn' t fuse during steel melting process. It has non- Wetability property throughout melting operartion It doesn't allow the liquid to pass through. It has easy smooth free fall on tapping The particles of Metafill remain free & non Sticky during the operation It doesn't have any chemical reaction with EBT basic refractory It doesn't cause any type of erosion of EBT refractories. Instructions Before Using METAFILL SP-I, the EBT should be totally cleaned. The slag pieces if any should be particularly removed from the EBT & it should be cleaned preferably with oxygen. METAFILL SP -I should be filled in pyramid fashion, or in dome shape. After theEBT is filled with METAFILL SP-I, the Gunning material which comes over there should also be cleaned. When the hot metal is charged from the back, the METAFILL SP – I gives best of Results. The Tapping Temperature also plays an important role for success of  the product. Packing The material of the grain size of 03 – 06 mm with special uniform Graphite coating is packed in 25 / 50 kgs. HDPE woven sack .

We have in store for our clients, a wide range of Green Flux Powder that is used in aluminum melting for covering, protecting & cleaning the molten metal. These fluxes should be used in 0.5 - 1 % of metal charge for crucible furnaces and 125 - 150 grams per sq. ft. for reverberatory furnaces. It is used for recovering Aluminum from the hot dross without melting again, which saves the cost of remelting. This flux and red hot dross are added alternately in sandwich fashion in the perforated vessel or bogie. The dross is stirred continuously every 15 minutes till no more metal falls through holes of vessel. The application rate of this flux is 5-10 %. Packing: 50 packets of 1 kg. Packed in 50 kgs. Double Polylined Hessian sacks, which is solid enough to withstand shakes and jolts of transportation.   More About Information of Green Cover Flux SP-V : It is used for recovering Aluminum from the hot dross without melting again, which saves the cost of remelting. This flux and red hot dross are added alternately in sandwitch fashion in the perforated vessel. The dross is stirred continuously every 15 minutes till no more metal falls through holes of vessel. The application rate of this flux is 5-10 %.

Our company is reputed as trader in the industry and situated in the well-connected area of Maharashtra(India). Ours is a renowned name in the field of supplying comprehensive array of Nozzle Filling Compound.

We are offering to our client DAFEX-11 ( Tundish Covering Compound ). These are offering as per client specification.. These are offering on market leading prices.   More About DAFEX – 21 (SP) is an extremely efficient insulatior, as soon as it is poured on molten metal . It expands almost five times and spreads immediately.if covers entire metal surface of the ladle and Tundish within few seconds. It prevents  hard crest formation on the ladle wall and reduces skulling near nozzles. The heat losses are negligible. Ladle dumps out clean metal, with no metal adhering to the refractory lining. There is no need to superheat metal prior to handing, thus extending furnance and ladle refractory life.while contributing to overall operating efficiency and imporved metallurgical properties. The exothermicity is mainatained throughoit the process. It is recommended to use this compound 2 kgs per ton of molten metal.

We are providing to our client DAFEX-21 (SP Ladle Covering Compound). These items are offering on market leading prices   More About DAFEX – II  a silica based insulating compound, acidic in nature, is specially formulated for use as a Tundish insulating cover in conventional casting . DAFEX – II an extremely efficient insulatior, medium exothermic which covers the entire metal surface in the Tundish. It prevents heat losses in the metal and reduces skulling near nozzles and ladle . Immediately after the addition it spreads on the metal surface and dry throughout the pour. Ladle dumps out clean metal with no metal adhering to the refractory lining.It is specially recommended for supersilica boards. There is no need to superheat metal prior to handling thus extending furnace and ladle refractory life while contributing to overall operating efficiency and improved metallurgical properties. Recommended use of this compound is 2 – 2.5 kgs, per ton of molten metal or 15 kgs epr meter square, depending on the size of ingots.

We have in store for our clients, a wide range of Green Flux Powder that is used in aluminum melting for covering, protecting & cleaning the molten metal. These fluxes should be used in 0.5 - 1 % of metal charge for crucible furnaces and 125 - 150 grams per sq. ft. for reverberatory furnaces. It is used for recovering Aluminum from the hot dross without melting again, which saves the cost of remelting. This flux and red hot dross are added alternately in sandwich fashion in the perforated vessel or bogie. The dross is stirred continuously every 15 minutes till no more metal falls through holes of vessel. The application rate of this flux is 5-10 %. Packing: 50 packets of 1 kg. Packed in 50 kgs. Double Polylined Hessian sacks, which is solid enough to withstand shakes and jolts of transportation.   More About Information of Green Cover Flux SP-V : It is used for recovering Aluminum from the hot dross without melting again, which saves the cost of remelting. This flux and red hot dross are added alternately in sandwitch fashion in the perforated vessel. The dross is stirred continuously every 15 minutes till no more metal falls through holes of vessel. The application rate of this flux is 5-10 %.

We are offering to our client DAFEX-11 ( Tundish Covering Compound ). These are offering as per client specification.. These are offering on market leading prices.   More About DAFEX – 21 (SP) is an extremely efficient insulatior, as soon as it is poured on molten metal . It expands almost five times and spreads immediately.if covers entire metal surface of the ladle and Tundish within few seconds. It prevents  hard crest formation on the ladle wall and reduces skulling near nozzles. The heat losses are negligible. Ladle dumps out clean metal, with no metal adhering to the refractory lining. There is no need to superheat metal prior to handing, thus extending furnance and ladle refractory life.while contributing to overall operating efficiency and imporved metallurgical properties. The exothermicity is mainatained throughoit the process. It is recommended to use this compound 2 kgs per ton of molten metal.

Degassers We are offering our clients with an appropriately prepared range of degassers that is used for degassing of Aluminum molten metal. This degassers gives the utmost degassing effect. It is used for all types of Aluminum and its different types of alloys. The application rate for this type of degasser is also about 0.2 %. Instructions After attaining the required metal temperature, shut off the furnace to have better degassing effect at falling temperature. Degasser tablet is to be slightly heated before use after removing the wrapper precaution is to be taken to avoid exposure of tablet to the atmosphere as it may pick up the moisture. Push the dross a little aside and plunge the recommended quantity of Daga Degasser using a preheated perforated bell plunger to the bottom of the melt. As soon as the bubbling stops remove the plunger after rabbling & skim off the dross. Advantages The use of Degasser is quite simple it does not require any special tool as equipment. It removes hydrogen gas, oxides and other impurities from the melt which results in superior finishing of the metal and avoids pinholes in the castings. Packing Daga Degasser are available in the shape of 50 Gms. & 250 Gms compact tablet form. The tablets are packed in 20 kgs & 40 kgs Box that is solid enough to withstand shakes and jolts of transportation.   More About Information of Degasser Tablets : Aluminium & its alloys are susceptible in absorbing gas even when the bestcontrolled melting processes are performed. There are many factors which cause absorption of Hydrogen gas like water vapour from atmosphere, damp scrap, damp tools, prolonged holding of metals etc. During the process of casting these unwanted gases release suddenly in the form of bubbles, which are trapped in the metal, and finally the development of pinhole porosity in the cast product occur. It is therefore necessary to remove the unwanted gas from the melt prior to pouring. DAGA DEGASSERS SP-II (Red) : Are formulated to remove hydrogen gas, oxides and other impurities from the melt which results in superior finishing of the metal and avoids pinholes in the castings It is used for all types of Aluminum and its different types of alloys. The application rate for this type of degasser is about 0.2 %. DAGA DGR SP-I (BLUE) : It is a very strong type of tablet, which is used for Degassing Aluminium and its alloys as well as Grain Refining also. Its application rate is about 0.2 %. Instructions : After attaining the required metal temperature, shut off the furnace to have better effect at falling temperature. DEGASSER or DGR tablet is to be slightly heated before use after removing the wrapper. The precaution is to be taken to avoid exposure of tablet to the atmosphere as it may pick up the moisture.Push the dross a little aside and plunge DEGASSER or DGR using a preheated perforated plunger to the bottom of the melt. As soon as the bubbling stops remove the plunger after rabbling, skim off the dross. Packing : DAGA DEGASSERS AND DAGA DGR’s are available in the shape of 50 Gms. & 250 Gms, packed in 25 kgs, 30 kgs & 40 kgs Boxes.

We are providing to our client DAFEX-21 (SP Ladle Covering Compound). These items are offering on market leading prices   More About DAFEX – II  a silica based insulating compound, acidic in nature, is specially formulated for use as a Tundish insulating cover in conventional casting . DAFEX – II an extremely efficient insulatior, medium exothermic which covers the entire metal surface in the Tundish. It prevents heat losses in the metal and reduces skulling near nozzles and ladle . Immediately after the addition it spreads on the metal surface and dry throughout the pour. Ladle dumps out clean metal with no metal adhering to the refractory lining.It is specially recommended for supersilica boards. There is no need to superheat metal prior to handling thus extending furnace and ladle refractory life while contributing to overall operating efficiency and improved metallurgical properties. Recommended use of this compound is 2 – 2.5 kgs, per ton of molten metal or 15 kgs epr meter square, depending on the size of ingots.