We offer a complete product range of LDPE Lupolen 2420 D Polyethylene, LDPE Lupolen 2420 H Polyethylene and LLDPE LL0209 AA Polyethylene

LDPE Lupolen 2420 D Polyethylene

Lupolen 2420 D is a non -additivated, low density Polyethylene.It is delivered in pellet form.

Applications :

Bags & Pouches
Bottles for Consumer Goods
Shrink Film
Blown Film

Film

Processing Method

Blown Film
Injection Moulding

Extrusion Blow Moulding

Features : Good Processability, Good Tear strength, Good Toughness

Specifications

Property	Value	Units	Test Method
Density	0.92	g/cm³	ISO 1183
Melt flow rate (MFR)(190^oC/2.16Kg)	0.25	g/10 min	ISO 1133
Tensile Modulus	240	MPa	ISO 527-1, -2
Tensile Stress at Yield	10	MPa	ISO 527-1, -2
Tensile Strength at Break MD/TD	27/20	MPa	ISO 527-1, -3
Tensile Strain at Break MD/TD	250/500	%	ISO 527-1, -3
Dart Drop Impact(50 blown film)	250	g	ASTM D 1709
Vicat softening temp(A50 (50 ^oC/h 10N))	94	^oC	ISO 306
Haze -50	<14	%	ASTM D 1103
Gloss (60^o,50)	>50	-	ASTM D 2457

View Complete Details

Ask Latest Price & Details

LDPE Lupolen 2420 H Polyethylene

Lupolen 2420 H is a non -additivated, low density Polyethylene.It is delivered in pellet form.

Applications :

Bags & Pouches
Film
Shrink Film
Blown Film

Cast Film

Processing Method :

Cast Film

Blown Film

Features : Good Heat Seal, Optical, Good Processability

Specifications

Property	Value	Units	Test Method
Density	0.92	g/cm³	ISO 1183
Melt flow rate (MFR)(190^oC/2.16Kg)	1.9	g/10 min	ISO 1133
Tensile Modulus	260	MPa	ISO 527-1, -2
Tensile Stress at Yield	11	MPa	ISO 527-1, -2
Tensile Strength at Break MD/TD	26/18	MPa	ISO 527-1, -3
Tensile Strain at Break MD/TD	250/600	%	ISO 527-1, -3
Dart Drop Impact(50 blown film)	110	g	ASTM D 1709
Vicat softening temp(A50 (50 ^oC/h 10N))	94	^oC	ISO 306
Haze -50	<8.0	%	ASTM D 1103
Gloss (60^o,50)	>100	-	ASTM D 2457

View Complete Details

Ask Latest Price & Details

LLDPE LL0209 AA Polyethylene

“LL 0209AA” is a LLDPE copolymer with butene as comonomer which contains antioxidant. It is recommended for general purpose applications. It is suitable for blending with conventional LDPE.

Film made from pure LL 02090 AA has the following advantages over conventional LDPE :

Better sealing, higher puncture resistance.
Greater drawdown capability.
Higher tensile strength.
Neutralizer : Calcium Stearate.
Antioxidant : Irganox1010, Irganox168

Applications :

Food Grade

Heave duty sacks, agricultural films, liners.

Produce bags, stretch film

Specifications

Property	Result	Value	Unit	Test Method
MFR ( 190^oC/2.16kg)	-	0.9	g/10min	ISO 1133
Density	-	920	Kg/m³	ISO 1183
Tensile Strength at Yield MD/TD	-	43384	MPa	ISO 527
Tensile Strength at Break MD/TD	-	41/32	MPa	ISO 527
Elongation at Break MD/TD	-	620/840	%	ISO 527
Tear Strength MD/TD	-	145/370	g/25μ	ASTM D1922
Dart Drop Impact	-	150	g	ASTM D1709