Contact SupplierType 430 Stainless Steel is a low carbon ferritic stainless steel which, in mildly corrosive environments or atmospheric exposures, has corrosion resistance approaching that of some nickel-bearing stainless steels. This alloy is oxidation resistant at elevated temperatures. Type 430 is ductile, does not work harden readily, and can be formed using a variety of roll forming or mild stretch bending operations as well as the more common drawing and bending processes. Type 430 is ferromagnetic.
Product Forms : Sheet, Strip
Specifications : ASTM A240
Typical Applications : Sinks, sink rims, appliance trim, counter tops, dish washers, range hoods, flatware, architectural uses, roofing, siding and restaurant equipment.
Processing : Type 430 should be annealed at 1450-1550ºF and furnace cooled at a rate of 50°F per hour to 1100°F and air cooled. If the annealing temperature does not exceed 1450°F (790°C), an air cool may be substituted for the furnace cool when annealing thin sections.
Forming : Type 430 is readily drawn and formed. Its drawing characteristics are similar to those of low-carbon steel, although it is stronger in the annealed condition and will require stronger tooling and increased power.
Welding : Type 430 is generally considered to be weldable by the common fusion and resistance techniques. Special consideration is required to avoid brittle weld fractures during fabrication. When a weld filler is needed, AWS E/ER 308L and 430 are most often specified. Corrosion: This alloy is resistant to attack in a wide variety of corrosive media including nitric acid, and many organic acids.
Element | Type 430 |
---|---|
Carbon | 0.12 max. |
Manganese | 1.00 max. |
Sulfur | 0.030 max. |
Phosphorus | 0.040 max. |
Silicon | 1.00 max. |
Chromium | 16.0 – 18.0 |
Nickel | 0.75 max. |
Type | Yield Strength 0.2% offset (KSI) | Tensile Strength (KSI) | % Elongation (2" Gauge length) | Hardness Rockwell |
---|---|---|---|---|
430 Ann | 30 min. | 65 min. | 22 min | HRB 89 |
Density (lb./ in^2) @ RT | 0.28 | |
---|---|---|
Modulus of Elasticity in Tension (psi x 10^6) | 29 | |
Specific Heat (BTU/oF/lb.) | 32 to 212 oF | 0.11 |
Thermal Conductivity (BTU/hr/ft^2/ft) | 212oF | 13.8 |
932oF | 15 | |
Mean Coefficient of Thermal Expansion (in. x 10^-6 per o F) | 32 to 212oF | 5.7 |
32 to 932oF | 6.2 | |
Electrical Resistivity (micro ohms - cm) | at 70oF | 60 |
Melting Point Range (oF) | - | 2600 - 2750 |
Oxidation Resistance - Continuous Service(oF) | - | 1500 |