Cement polymer based tile grout, for Construction Use, Grade : 37

Listing ID #5521687

Tile grouts are generally of polymer modified cementitious or epoxy resin based. It should be flexible in nature should accommodate movements and also should not shrink like white cement. It should have a good bond with all types of tiles, thus making joints impermeable to water. In situations where non-toxic, chemical resistant properties for tile joint filler are required especially in food and pharma industry, epoxy resin based is the ideal solution.

Features and benefits :

• For grout joints between 2 mm to 8 mm.
• Easy to mix, creamy consistency and high productivity grout.
• Can be applied on the wall and floor

Instruction for use : 

• Grouting should not begin until the tilesetting material is properly cured (a minimumof 24 hours).
• Wipe the tile surface with a damp clothbefore grouting.
• Using a Float, trowel the mixed grout over thesurface and into the grout joint, careful to assure alljoints are filled fully. Hold the float at a 45O angle to the surface of the tile.
• As soon as possible, remove excess grout from the tile surface with float held at a 90O angle and moving diagonally across the joints. Strike the joint with the blunt end of a tool-compacting the surface but not digging out the grout.
• Clean remaining grout from the tile surface as soonas grout firms up enough to be worked without being pulled from the joint by using a Scotch Bright Pad,or a pad of dampened cheese cloth or tile cleaner.Under extreme heat or low humidity conditions, the floor should be covered with brown Kraft paper to retain moisture. Do not use polyethylene as it may resultin uneven drying and discolored joints. The grouted floor must be protected from traffic for 72 hours after installation.