The manufacturing process in nutshell can be described as under:
The structural steel grating for galvanizing are procured.
The steel articles are dipped into "Caustic Soda Solution" for "Degreasing"
The load is rinsed in "Rinsing Tank" containing clean water
The load is then preserved in "Pickling Tank" containing HCL 10-12% for first pickling
Second pickling is performed in "Second Pickling Tank" which contains HCL - 10-32%
The load is again rinsed in "Rinsing Tank" containing clean water
Next step is "Pre-fluxing" wherein the material is dipped in "Pre-Fluxing" tank containing "Zinc Ammonium"
The load is then dipped into molten zinc at 440-460 degree Celsius which is termed as "Hot Dip Galvanizing"
The material then is "Quenched" by passing through running water
The material is due for dispatch after "Passivation" and inspection formalities

The manufacturing process in nutshell can be described as under:
The structural steel grating for galvanizing are procured.
The steel articles are dipped into "Caustic Soda Solution" for "Degreasing"
The load is rinsed in "Rinsing Tank" containing clean water
The load is then preserved in "Pickling Tank" containing HCL 10-12% for first pickling
Second pickling is performed in "Second Pickling Tank" which contains HCL - 10-32%
The load is again rinsed in "Rinsing Tank" containing clean water
Next step is "Pre-fluxing" wherein the material is dipped in "Pre-Fluxing" tank containing "Zinc Ammonium"
The load is then dipped into molten zinc at 440-460 degree Celsius which is termed as "Hot Dip Galvanizing"
The material then is "Quenched" by passing through running water
The material is due for dispatch after "Passivation" and inspection formalities