Contact Supplier| Material | N66 | PTFE | PVDF |
|---|---|---|---|
| Product | N66 Membrane | PTFE Membrane Filter | PVDF Membrane Filter |
| Filter Media | N66 | PTFE | PVDF |
| Dimension Size (mm) | Ǿ47mm | Ǿ47mm | Ǿ47mm |
| Filtration Precision | 0.45um | 0.45um | 0.45um |
| Test Liquid | Water | Alcohol | Alcohol |
| Test Temperature | 20oC | 20oC | 20oC |
| Test Standard | QB/KN002-2007 | QB/KN002-2007 | QB/KN002-2007 |
| Appearance | Good | Good | Good |
| Thickness | 0.115mm-0.125mm | 0.16mm-0.24mm | 0.10mm-0.115mm |
| Flow Rate (Pure Water) | 18.1mL/cm2.min- 21.7mL/vm2.min | 40.2mL.cm2.min- 44.6mL/cm2.min | 28.7mL/cm2.min- 31.9mL/cm2.min |
| Bubble Point (Mpa) | >-0.20 Mpa | >-0.05 Mpa | >-0.06 Mpa |
| Material | PES | |
|---|---|---|
| Product | Polyether Sulphone Membrane Filter | |
| Thickness | 110um (+_10um) | |
| Bubble Point (Water) | Pore Size (1.2-0.1um) | Bubble Point (water) (105-280 kPa) |
| Chemical Compatibilty | Resist again hydrophilic liquid : stable among the pH4-8 | |
| Extractables with water | <0.2% | |
| Breakthrough | Pore Size (1.2-0.1um) | M3/m2.hr.bar(>-2.4-156) |
| Heat Stability | Maximum Temperature- 130oC | |
| Sterilization Method | Autoclaving (121oC), y-ray or Epoxy Ethane Suffocating | |