Details :

• All purpose. low temperature flux for use in brazing both ferrous and non-ferrous metals and alloys using silver brazing filler metals. Begins to melt and dissolve oxides of 340'C. Fully molten at about 600'C and provides adequate protection upto 750-'C Excellent in hat rodding operation used to braze weld where the hat brazing rod is pluged into the dry powder. Easy cleanup in hot water.
• For application where a dry low volatile flux is required. Recommended for use in 650-815°C range. Excellent in hot rodding operations. Easy Cleanup.
• General purpose, law temperature flux which provides excellent and creamy smooth consistency. For brazing all ferrous and non-ferrous alloys. Beging to melt and dissolves oxides at 326G, fully malten at 600"C. It Provides excellent protection of parts upto 870°C. Easy cleanup with hot water.
• For brazing high chromium stainless steels. tungsten and chromium carbides, and molybdenum alloys. its temperature range is 600-9250C and it is useful in applications where local overheating may occur, as in fast induction heating. Boron Modified.
• For applications with long heating cycles as in furnace brazing. Also useful in induction operations, where tendency to overheat moy exist. Active range : 650-870°C

• Used where brazing temperatures go into the 870-1100°C range or for considerable length of time above 785oC

Details :

• All purpose. low temperature flux for use in brazing both ferrous and non-ferrous metals and alloys using silver brazing filler metals. Begins to melt and dissolve oxides of 340'C. Fully molten at about 600'C and provides adequate protection upto 750-'C Excellent in hat rodding operation used to braze weld where the hat brazing rod is pluged into the dry powder. Easy cleanup in hot water.
• For application where a dry low volatile flux is required. Recommended for use in 650-815°C range. Excellent in hot rodding operations. Easy Cleanup.
• General purpose, law temperature flux which provides excellent and creamy smooth consistency. For brazing all ferrous and non-ferrous alloys. Beging to melt and dissolves oxides at 326G, fully malten at 600"C. It Provides excellent protection of parts upto 870°C. Easy cleanup with hot water.
• For brazing high chromium stainless steels. tungsten and chromium carbides, and molybdenum alloys. its temperature range is 600-9250C and it is useful in applications where local overheating may occur, as in fast induction heating. Boron Modified.
• For applications with long heating cycles as in furnace brazing. Also useful in induction operations, where tendency to overheat moy exist. Active range : 650-870°C

• Used where brazing temperatures go into the 870-1100°C range or for considerable length of time above 785oC