Contact SupplierManufactured from virgin high performing special grade raw material PE-80 & PE-100.
State-of-the art machinery producing high quality pipes.
With Phase-I and Phase-II approval.
Minimum required strength (MRS) of 8 MPa & 10 MPa.
Suitable for working pressure up to 7.0 bar.
Wide range starting from 20mm to 355mm OD.
50, 100 and 150m coils up to size 110mm.
6m length on all sizes above 110mm.
Specification conforming to IS-14885 & ISO 4437 - SDR17.6, 13.6, 11 & 9.
High resistance to chemical reaction.
Light weight and flexible.
Easy handling and jointing leading to reduced cost.
Easy repair in the event of damage.
No outer painting required.
Very low maintenance cost.
Very low friction.
Outstanding ability to withstand Rapid Crack propagation (RCP).
High resistance to Crack Growth.
Very high abrasion resistances.
Tie-up with Fusion Provida, UK
Fittings manufactured from PE-80 & PE-100 special grade raw materials
Recognized by British Gas PIC, Australian Gas Authorities. DVGW-Germany and many gas authorities all over the world
Wide range of fittings from 20mm to 355mm
Universally adopted Pin-configuration to match with any EF welding machine
Manual and Bar code-both options provided on each fittings.
Operating voltage 40 ± 0.5V (other options available on request).
Natural Gas/ Vaporized LPG Conveyance and Distribution.
Industrial Gases Distribution
Landfill & Leachate Gas Extraction and Conveyance
Gas distribution and water distribution systems.
Jain Polyethylene Gas Pipe are suitable for Gas distribution network both for domestic & industrial consumption.
PE-100 SDR 7 & 9 are suitable for use in cross country gas conveyance pipeline systems.
Srl | Property | Units | Requirements | Test Parameters | Test Method |
01 | Wall Thickness | mm | PE - 80 & PE -100 SDR series | - | ISO-3126 |
02 | Hydrostatic Strength (HS) | h | Failure time > 100 h | PE-80-9.0 MPa-20ºC | ISO-1167 |
Failure time > 165 h | PE-80-4.6 MPa-80ºC | ||||
Failure time > 1000 h | PE-80-4.0 MPa-80ºC | ||||
03 | Elongation at Break | % | ≥ 350 | - | ISO-6259/3 |
04 | Density | Kg/m³ | ≥ 930 | 23ºC | ISO-1183 ISO-1872/1 |
05 | Thermal Stability (Oxidation Induction Time) |
Min. | ≥ 20 | 200ºC | ISO TR10837 |
06 | Melt Flow Rate | 9/10 Min | 0.2 to 1.1 | 190ºC 5 Kg | ISO-4440/1 |
07 | Tensile Strength | MPa | 15 Min | 23ºC | IS: 14885 |
08 | Elongation at Break | % | 350 Min | 23ºC | IS: 14885 |