Stainless Steel DIN 1.4301 / 1.4306 / 1.4307 Sheets & Plates Supplier
We are Manufacturing & Exporting of high quality stainless steel 304 sheets, stainless steel 304L plates, stainless steel 304 coils in thickness of 0.3mm to 120mm. that have found extensive applications in various industries. We also deal in Nickel and copper alloy, Stainless & Duplex Steel, Carbon & Alloy Steel, are the materials which are used for designing of stainless steel sheet, plate and coil. We offer various grades of stainless steel plates & Stainless Steel Sheets link ss 310 plates, ss 317 sheets & ss 321 plates etc.
| Standards | Designation |
|---|---|
| ASTM | A 240 |
| ASME | SA 240 |
| Grade | C | Mn | Si | P | S | Cr | Mo | Ni | N | |
| 304 | min. max. | - 0.08 | - 2.0 | - 0.75 | - 0.045 | - 0.030 | 18.0 20.0 | - | 8.0 10.5 | - 0.10 |
| 304L | min. max. | - 0.030 | - 2.0 | - 0.75 | - 0.045 | - 0.030 | 18.0 20.0 | - | 8.0 12.0 | - 0.10 |
| 304H | min. max. | 0.04 0.10 | - 2.0 | - 0.75 | -0.05 | - 0.030 | 18.0 20.0 | - | 8.0 10.5 | - |
| Grade | Tensile Strength (MPa) min | Yield Strength 0.2% Proof (MPa) min | Elongation (% in 50mm) min | Hardness | |
| Rockwell B (HR B) max | Brinell (HB) max | ||||
| 304 | 515 | 205 | 40 | 92 | 201 |
| 304L | 485 | 170 | 40 | 92 | 201 |
| 304H | 515 | 205 | 40 | 92 | 201 |
| Grade | Density of ss304 in kg/m3 | Elastic Modulus (GPa) | Mean Coefficient of Thermal Expansion (μm/m/°C) | Thermal Conductivity (W/m.K) | Specific Heat 0-100°C (J/kg.K) | Electrical Resistivity (nΩ.m) | |||
| 0-100°C | 0-315°C | 0-538°C | at 100°C | at 500°C | |||||
| 304/L/H | 8000 | 193 | 17.2 | 17.8 | 18.4 | 16.2 | 21.5 | 500 | 720 |
| Grade | UNS No | Old British | Euronorm | Swedish SS | Japanese JIS | ||
| BS | En | No | Name | ||||
| 304 | S30400 | 304S31 | 58E | 1.43 | X5CrNi18-10 | 2332 | SUS 304 |
| 304L | S30403 | 304S11 | - | 1.43 | X2CrNi19-11 | 2352 | SUS 304L |
| 304H | S30409 | 304S51 | - | 1.49 | X6CrNi18-11 | - | - |
These comparisons are approximate only. The list is intended as a comparison of functionally similar materials not as a schedule of contractual equivalents. If exact equivalents are needed original specifications must be consulted.
| Grade | Why it might be chosen instead of 304 |
|---|---|
| 301L | A higher work hardening rate grade is required for certain roll formed or stretch formed components. |
| 302HQ | Lower work hardening rate is needed for cold forging of screws, bolts and rivets. |
| 303 | Higher machinability needed, and the lower corrosion resistance, formability and weldability are acceptable. |
| 316 | Higher resistance to pitting and crevice corrosion is required, in chloride environments |
| 321 | Better resistance to temperatures of around 600-900°C is needed…321 has higher hot strength. |
| 3CR12 | A lower cost is required, and the reduced corrosion resistance and resulting discolouration are acceptable. |
| 430 | A lower cost is required, and the reduced corrosion resistance and fabrication characteristics are acceptable. |