Contact SupplierWe are offering stainless steel composite panel for our esteemed clientele. The stainless steel composite panel comes with a non-combustible mineral-filled core, which is used as an exterior cladding for elevations, canopies, columns and for extravagant interior applications. It can also be used in fitouts for staircases, elevators & escalators. The core used in this composite panel is fire retardant magnesium oxide. Surface is protected with a self-adhesive peel - off protective film. Under normal outdoor weather conditions, the protective film can withstand 25 to 40 days exposure without its original peel-off characteristic after which time film must be removed.
tosolbond ssc (stainless steel top skin + polyethylene core + stainless steel bottom skin)
tosolbond ssc fr (stainless steel top skin + polyethylene core + stainless steel bottom skin)
product detailscompositiontosolbond ssc is composed for non - combustible mineral filled core sandwiched between two skins of 0.3 mm / 0.4 mm thick stainless steel in sus 316 or sus 304.top skin material0.3 /0.4 mm thick stainless steel sus 316 or sus 304 stainless steel sheet.core materialnon - combsutible mineral core or polyethylene core.bottom skin material0.3 /.4 mm thick stainless steel, sus 316, sus 304, sus 430 or aluminium skin. The core used in this product is fire retardant magnesium oxide. Surface is protected with a self-adhesive peel - off protective film. Under normal outdoor weather conditions, the protective film can withstand six month's exposure without long its original peel-off characteristic after which time film must be removed.surface finishhairline finish, dull finish, mirror finish
dimensionspanel thickness4 mmpanel sizewidth =1220 mm
length = less than 2440 mm or upto 3000 mm maximum.
tolerancewidth+- 2.0 mmlength+- 4.0 mmthickness+-0.2 mmsquarenessmaximum 5.0 mm.
Panel weight | 10.5 kg/m2 if 0.3 mm skin is used |
---|---|
Length | 11.o kg/m2 if 0.4 mm skin is used |
Thermal Properties | - |
Thermal expanision 10 degree / C | 15.9 @ 125 degree C |
Thermal Conductivity w/m-k | 16.2 @125 degree C |
Deflection temperature | 120 degree C |
Sound transmission loss | 30 STC (Sound Transmission Class) |
Hardness (Rockwell B) | 79 |
---|---|
Tensile Strength (Yield) | 290 Mpa |
Tensaile Strength (Ultimate) | 580 Mpa |
Elongation | 28 % |
Flexural Elascticity - E | 140.8 Gpa |
Poisson's Ratio | 0.27 - 0.30 " 25 degree C |