Contact SupplierSlow Speed Revolving Centers body made from alloy steel EN-32B and Case Hardened & tempered to a hardness of 32-40 HRc approx.
Majority of sizes have point made from EN-31 and htorugh hardened to 60 HRc approx. for max. wear resistance.Very large sizes have points made from alloy steel 20MnCr5 and case hardened to 55-58 HRc to impart resistance against shearing under very heavy loads.
| M.T. No. | STYLE | Od mm | OD mm | OD1 mm | L1 mm | L2 mm | L mm | RATED LOAD AT 100 rpm. Kg | |
|---|---|---|---|---|---|---|---|---|---|
| AXIAL | RADIAL | ||||||||
| MT -2 | A | 23 | 50 | 17.78 | 30 | 61 | 64 | 300 | 200 |
| MT - 3 | A | 30 | 62 | 23.83 | 38 | 70.5 | 81 | 600 | 400 |
| MT - 4 | A | 30 | 62 | 31.27 | 38 | 73.5 | 102.5 | 800 | 600 |
| MT - 5 | A | 34 | 68 | 44.4 | 42 | 78 | 129.5 | 1100 | 850 |
| MT - 6 | A | 50 | 105 | 63.35 | 58 | 91 | 182 | 2100 | 1500 |