Low Cement Castable, Purity : 100%

Product Details

Product	Max.Service Temp.	Water Reqd.For Casting	Chemical Analysis		Physical Properties				Thermal Properties
-	-	-	Al2o3 % Min.	Fe2o3 % Max.	Density After Drying At 110 °C/ 24hrs	Ccs Kg/Cm2 After Drying At 110 °C / 24hrs	Ccs Kg/Cm2 Afterheating At 1100 °C / 3hrs	Ccs Kg/Cm2 Afterheatingat 1550 °C / 3hrs	Pce Oc/°C	Plc3 Hrs
-	-	-	Al2o3 % Min.	Fe2o3 % Max.	Density After Drying At 110 °C/ 24hrs	Ccs Kg/Cm2 After Drying At 110 °C / 24hrs	Ccs Kg/Cm2 Afterheating At 1100 °C / 3hrs	Ccs Kg/Cm2 Afterheatingat 1550 °C / 3hrs	Pce Oc/°C	1100	1550
Rr Lc - 45	1550 °C	6.0 - 6.5%	0.45	0.01	2.3gm/Cc	600	850	1000	32/1717	-0.15	-1.50 / 1500
Rr Lc - 60	1600 °C	5.5 - 6.5 %	0.6	0.015	2.5gm/Cc	700	850	1000	36/1804	-0.12	-0.75
Rr Lc - 70	1650 °C	4.5 - 5.5 %	0.7	0.016	2.65gm/Cc	700	875	900	36/1804	-	1.25
Rr Lc - 70 (LI)	1650 °C	4.5 - 5.5 %	0.7	0.01	2.60gm/Cc	600	850	900	36/1804	-	1.37
Rr Lc - 80	1700 °C	4.5 - 5.5 %	0.8	0.02	2.85gm/Cc	750	950	1200	37/1820	0.25	1.4
Rr Lc - 90	1750 °C	4.5 - 5.5 %	0.9	0.0125	3.00gm/Cc	850	1050	1250	+37/1820+	0.25	1.5