Leading Manufacturer, Supplier & Retailer of Refractory Mortar.
Fire Clay & High Alumina Refractory Mortar
| Quality | Al203 (%) | Fe203 (%) | PCE Orton Cone (°C) | Service Temp (°C) | Application Area |
|---|---|---|---|---|---|
| DATCAST -Mortar-IS-6 | 24 | 2.5 | 20 / 1564 | 1350 | For laying of 30% Al203 bricks |
| DATCAST -Mortar-HHD | 26 | 2.5 | 26 / 1621 | 1400 | For laying of 35% Al203 bricks |
| DATCAST -Mortar-40 | 38 | 3.5 | 30/ 1665 | 1450 | For laying of 40% Al203 bricks |
| DATCAST-Mortar-45 | 43 | 2.8 | 311/2 / 1699 | 1500 | For laying of 45% Al203 bricks |
| DATCAST -Mortar-50 | 48 | 4 | 31 / 1683 | 1500 | For laying of 50% Al203 bricks |
| DATCAST -Mortar-60 | 55 | 3.5 | 32 / 1717 | 1550 | For laying of 60% Al203 bricks |
| DATCAST -Mortar-70 | 65 | 3.5 | 33 / 1743 | 1600 | For laying of 70% Al203 bricks |
| DATCAST -Mortar-80 | 75 | 3.5 | 35 / 1783 | 1700 | For laying of 80% Al203 bricks |
| DATCAST -Mortar-85 | 80 | 2 | 36 / 1804 | 1750 | For laying of 85% Al203 bricks |
Air Setting Refractory Mortar
| Product / Type / Nature of Bond | DATSET-50 NORMAL 50% Alumina Mortar (Coarse) Chemical/ Ceramic | DATSET-50 Fine 50% Alumina Mortar (Fine) Chemical/ Ceramic |
|---|---|---|
| GENERAL PROPERTIES | ||
| Raw Material Base | Calcined Bauxite | Calcined Bauxite |
| Max. Service Temperature | 15000C | 15000C |
| Sintering Temperature | 11000C | 11000C |
| Maximum Grain Size | 1.5 mm | 0.5 mm |
| CHEMICAL ANALYSIS, % | Specification | Specification |
| Al2O3 | 49 min. | 49 min. |
| Fe2O3 | 4 max. | 4 max. |
| PHYSICAL PROPERTIES | Specification | Specification |
| Water for | - | - |
| Trowelling Consistency, % | 24-28 | 24-28 |
| Water Required for | - | - |
| Ramming Consistency, % | 43385 | 43385 |
| Transverse Strength, Kg/cm2 | - | - |
| After Drying At 100°C/24 Hrs. | 17 | 23 |
| % Ratained Above Maximum size | 5 max | 5 max |
| THERMAL PROPERTIES | Specification | Specification |
| Pyrometric Cone Equivalent, Orton/°C | 31/1683 min | 31/1683 min |