We are leaders in the market for providing best range of Aluminium Clad Steel Wire

Aluminium Clad Steel Wire

Conductivity Tensile Strength
20.3% IACS 1, 340 N/min2max.
27% IACS 1, 080 N/min2max.
30% IACS 880 N/min2max.
40% IACS auf nachfrage 680 n/min2

Description :

ACS = (Aluminium Clad Steel) is a high strength steel wire with a thick aluminium coating.
Aluminium Clad Steel (ACS) wire consists of a central steel core with a layer of highconductivity aluminium extruded over it. The aluminium layer forms a seamless metallurgical tie with the steel wire to guarantee permanent bonding during rewinding and stranding.
The aluminium layer thickness is atleast 10% of the wire radius and approximately 25% of the cross-sectional area. Conductivity is proportional to the aluminium layer thickness. Conductivities ranging from 20% to 40% IACS are available.
Aluminium Clad Steel cable is well known for its combination of corrosion resistance, high strength and superior electrical conductivity. These properties make it an excellent choice either as overhead static wire (ground wire, OPGW) It can also be used as core in ACSR conductors.

ASTM B52 10

ASTM B52-10 (2007) ASTM Standard specification for Aluminum-Clad Steel Wire, Aluminum Conductors, Aluminum-Clad Steel Reindorced.

ASTM B502

This specification covers round, aluminum-clad steel core wire used for mechanical reinforcementin the manufacture of aluminum conductors, aluminum-clad steel reinforced. The base metal shall be steel produced by the openhearth, electric furnace, or basic-oxygen.

Applications :

	Higher mechanical tensile strength
	Higher continuous tensile strength
	Higher conductivity
	Reduction of performance losses
	Less weight
	Less sag
	Retains strength

Item	Tensile Strength	Coefficient of Linear Expansion	Modulus of Elasticity	Applied Condustors
Galvanized INVER Wire	105~110	2.8	16,500	STACIR
Al-clad INVER Wire	105~110	3.7	15,500	STACIR/AW
High-Strength Al-clad Inver Wire	120~125	3.7	15,500	Hi-STACIR/AW