Our Products
Ferro Niobium is an alloy of iron and niobium with niobium content above 60% by weight. It is an additive in production process of amorphous metals. It imparts corrosion resistance and makes the alloy much stronger and weldable. It increases high temperature resistance, oxidation resistance, creep resistance, it also reduces erosion at high temperatures. It is used in application that needs to handle larger stress and needs good strength to weight ratio.
Applications:
Graph
Grade | Nb % | C % Max. | S % Max. | P % Max. | Si % Max. | Al % Max. |
---|---|---|---|---|---|---|
FNB – 01 | 60 – 70 | 0.1 | 0.05 | 0.1 | 1 | 3 |
FNB – 02 | 65 -75 | 0.1 | 0.05 | 0.05 | 1 | 2 |
Ferro Titanium is an alloy of iron and titanium with titanium content ranging from 20 % to 75%. It is used as cleansing agent for iron and steel as it is highly reactive to sulfur, oxygen, carbon and nitrogen. It is used in stainless steel as a stabilizer to prevent chromium carbide formation at grain boundaries.
Application:
Graph
Grade | Ti % | C % Max. | S % Max. | P % Max. | Si % Max. | Al % Max. |
---|---|---|---|---|---|---|
FTI – 01 | 35-40 | 0.1 | 0.05 | 0.05 | 2 | 10 |
FTI – 02 | 40-45 | 0.1 | 0.05 | 0.05 | 2 | 10 |
FTI – 03 | 60-65 | 0.2 | 0.05 | 0.05 | 1 | 5 |
FTI – 04 | 68-75 | 0.2 | 0.05 | 0.05 | 1 | 5 |
Ferro Vanadium is an alloy of iron and vanadium with vanadium content of more than 50% by weight. It improves the strength of steel and makes it suitable for use in high strength structural steel. It is also used in manufacturing of crude steel as it improves the tensile strength and is light weight owing to its density. Vanadium when added to steel gives it stability against alkalis, hydrochloric acid and sulfuric acid.
Application:
Grade
Grades | V % | C % Max. | S % Max. | P % Max. | Si % Max. | Al % Max. |
---|---|---|---|---|---|---|
FV-01 | 60-65 | 0.1 | 0.05 | 0.1 | 1.5 | 2 |
FV – 02 | 65- 75 | 0.1 | 0.05 | 0.1 | 1.5 | 2 |
FV – 03 | 75 – 85 | 0.1 | 0.05 | 0.1 | 1.5 | 2 |
Ferro Molybdenum is an alloy of iron and molybdenum with molybdenum content of more than 60% by weight. It is used as hardening agent and increases corrosion resistance of steel. It is added to molten steel before casting.
Applications:
Grade
Grade | Mo % | C % Max. | S % Max. | P %Max. | Si % Max. | Cu % Max |
---|---|---|---|---|---|---|
FMO-01 | 60-65 | 0.1 | 0.05 | 0.05 | 1 | 0.5 |
FMO-02 | 65-68 | 0.1 | 0.05 | 0.05 | 1 | 0.5 |
FMO-03 | 68-75 | 0.1 | 0.05 | 0.05 | 1 | 0.5 |