Round Ceramic Balls, For Chemical Factory, Industry, Purity : 99%

Get Latest Price

MaterialCeramics
Purity99%
Hardness0-25HRC
ShapeRound
Supply TypeManufacturer, Exporter, Supplier, Retailer
Preferred Buyer Location All over the world

View More Details

Send Enquiry

Company Information

N. Gandhi & Co

Subhash Road, Mumbai, Maharashtra

4.6/5

(30)

View Number

Member Since 20 Years
Nature of Business Retailer
GST No. 27AADFN2634E1ZK

Ask for more detail from the seller

Contact Supplier

Report incorrect details

View Company Details

Product Details
Company Details

MaterialCeramics
ShapeRound
ApplicationChemical Factory, Industry
Purity99%
Hardness0-25HRC
Softening Point0-1000 Deg C
FeaturePrefect Shape, Variegated Dried

Our company is widely known in the market for supply of top quality, durable Ceramic Balls. These are used as raw materials along with the calcined ceramics. Available at competitive prices, our range of ceramic balls feature abrasion resistance, toughness and are very light weight making them high on utility and functionality factor.

Si3N4 Silicon Nitride(Physical Properties)

Structure	Multi-Crystal
Chemical Formula	Si₃N₄
Purity %	95,00
Density g/cm	3,20
Operating Temperature^oC	1100
Melting Point	1900^oÑ
Softening Point	100^oÑ
Specific Heat at 25° C (cal/g/° C) Thermal Conductivity	0,17 29 W/m° K

Mechanical Properties

Vickers Hv10 Hardness (N/mm²)	24000
Modulus of Elasticity (N/mm²)	3,1õ105
Breaking Modulus at 25^oC (N/mm²)	700
Compressive Strength at 25^oC (N/mm2)	2500

Al2O3 99, 55% Alumina(Alumina Oxide) (Physical Properties)

Structure	Multi-Crystal
Chemical Formula	ÀL₂Î₃
Purity %	99,8
Density g/cm	3,90
Operating Temperature ^oC	1800
Melting Point	2050^oC
Softening Point	1725^oÑ
Specific Heat at 25^oC (cal/g/^oC) Thermal Conductivity	0,25 29 W/m^o K

Mechanical Properties

Vickers Hv10 Hardness (N/mm²)	16500
Modulus of Elasticity (N/mm²)	3,5õ105
Breaking Modulus at 25° C (N/mm²)	470
Compressive Strength at 25° C (N/mm²)	2354

ZrO2 ZIRCONIUM OXIDE(Physical Properties)

Structure	Multi-Crystal
Chemical Formula	ZrO₂
Purity %p	97,00
Density g/cm	5,50
Operating Temperature ^oC	1000
Melting Point	-
Softening Point	-
Specific Heat at 25^o C (cal/g/^o C) Thermal Conductivity	9 W/m^oK

Mechanical Properties

Vickers Hv10 Hardness (N/mm²)	20000
Modulus of Elasticity (N/mm²)	2õ105
Breaking Modulus at 25^oC (N/mm²)	600
Compressive Strength at 25^oC (N/mm²)	2100

Al2O3 99, 99% RUBY(Physical Properties)

Structure	Single Crystal
Chemical Formula	ÀL₂Î₃
Purity %	99,99
Density g/cm	3,99
Operating Temperature^oC
Melting Point	2050^oC
Softening Point	1800^oC
Specific Heat at 25^oC (cal/g/^oC) Thermal Conductivity	0,18 36 W/m^oK

Mechanical Properties

Vickers Hv10 Hardness (N/mm²)	17000
Modulus of Elasticity (N/mm²)	4,3õ105
Breaking Modulus at 25^oC (N/mm²)	392
Compressive Strength at 25^oC (N/mm²)	2060

Al2O3 99, 99% SAPPHIRE(Physical Properties)

Structure	Single Crystal
Chemical Formula	ÀL₂Î₃
Purity %	99,99
Density g/cm	3,99
Operating Temperature^oC
Melting Point	2050^oC
Softening Point	1800^oC
Specific Heat at 25^oC (cal/g/^oC) Thermal Conductivity	0,18 36 W/m^o K

Mechanical Properties

Vickers Hv10 Hardness (N/mm²)	17000
Modulus of Elasticity (N/mm²)	4,3õ105
Breaking Modulus at 25^oC (N/mm²)	392
Compressive Strength at 25^oC (N/mm²)	2060